Our ICT Guy here at my company loves to use lots of via holes as test points - via holes which are 0.040" diameter, and spaced at 0.004" edge to edge spacing! He doesn't like to tent the via's either, so I always battle via-to-via shorts at the wave
Electronics Forum | Mon Jan 15 11:41:56 EST 2007 | davef
Questions are: * Does the component take solder when you dip it in the solder pot to test the solderability of the leads? * Can you get full barrel fill when wave soldering a bare board? * Is your flux reaching the top of the board through the hole b
Electronics Forum | Fri Mar 26 11:31:34 EDT 2010 | rway
I have been using ICT for a number of years. It is still a viable resource for catching defects in the production process. AOI doesn't catch everything, such as bridging on QFN or J-lead devices (this will depend on the type of AOI and camera syste
Electronics Forum | Tue Mar 07 21:35:16 EST 2006 | Cal Kolokoy
Samir, From experience, the only board test situation where tented via's have difficulty with contact is with a Flying Probe type tester. Otherwise, for traditional ICT, the force of the pogo pins, correct probe type, and fixture design should do th
Electronics Forum | Mon Apr 09 20:55:46 EDT 2012 | action_101
I forgot to add that we are using a 3 mil stencil. It seems like to me that may be there isn't enough flux left when we reach liquidous?? About half of the solder spheres do melt and wet on each pad, but the top half of each solder joint is just the
Electronics Forum | Thu Feb 12 11:57:59 EST 2009 | jmiller
i have searched the forum for hours. read all the threads that deals with cleanliness and ionic testing. (http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=40295) (http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=22603) (http://www.
Electronics Forum | Tue Nov 06 22:37:35 EST 2012 | davef
Ryan ... "As for bismuth-based lead-free alloys, a lower melting temperature than that of tin-lead is offered together with a cost similar to that of tin [in the area of $3/lb]. Unfortunately, bismuth in soldering alloys tends to create embrittlemen
Electronics Forum | Mon Jan 15 09:19:29 EST 2007 | tk380514
We use Alpha EF-2202 low-VOC No-Clean flux Selective wave soldering cassettes Bottom pre-heating wave soldering machine We have one component that will not solder properly: http://www.epcos.com/web/generator/Web/Sections/ProductCatalog/Capacitors/Ul
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Wed Feb 10 05:23:17 EST 2021 | karl_willoughby
Hello. I am sourcing machines for an SMT line (for the first time) and would like to understand features of current and earlier model SPI and AOI machines. In the intended application, a high volume of PCAs aren't required to be processed but there