Electronics Forum | Mon Feb 20 15:03:56 EST 2006 | davef
Q1- Will we be able to select the materials (flux and alloy) and run the process depending only on ourselves, distributors� help, machinery documentation, web data and �trial and error?� A1- Your materials suppliers [eg Kester, Alpha Metals, etc] wil
Electronics Forum | Thu Feb 16 13:06:49 EST 2006 | masrimhd
Hello, We�ve ordered the line machinery for our TV factory. It should be ready after two to three months. We will start producing Analog CRT TVs using single sided FR2 or CEM1, thru-hole components and tin-lead wave soldering process. Knowing that
Electronics Forum | Wed Dec 31 08:45:16 EST 2003 | tommy
We started up with the temperature recording daily and change it to once per week.The calibration is done 6 monthly and again it depend on usage,product thermal sensitivity and customer requirement.
Electronics Forum | Wed Jan 28 08:47:08 EST 2004 | solderboffin
No problem Chava. I need you email address. send me an email and I will forward it to you. Nick. Nick Prince Coopertools Europe. http://www.cooperhandtools.com/europe/
Electronics Forum | Fri May 12 07:53:40 EDT 2006 | egrice1
Sheldon, Tip life is directly related to temperature, IRON plating thickness on the tip, Alloy composition used and operator technique. High tin contents in lead free alloys attach the tips. Poor wetting and higher melting temperatures cause us
Electronics Forum | Fri Jan 02 05:40:20 EST 2004 | p.LAKSHMANAN
cALIBRATION OF SOLDERING IRON DEPENDS ON THE USAGE AND AGAIN DEPENDS ON THE PERFORMANCE.NORMALLY U CAN FIX THE CALIBRATION INTERVAL AS 3 MONTHS (OR) 6 MONTHS AND ANALYSE IF THERE IS ANY SUBSTANTIAL DRIFT IN THE READINGS(BETWEEN ACTUAL AND DISPLAYED).
Electronics Forum | Thu Jan 22 15:37:04 EST 2004 | solderboffin
Hi Vijay The short answer is, there isnt one! Sorry to be vaugue but its pretty much up to you and the quality systems you are working to. The generally accepted interval is every month, but there are not rules. The other issue to face is the defini
Electronics Forum | Tue Nov 15 16:31:04 EST 2011 | pcbrown
Can anyone tell me if the Metcal SP200 solder station meets the J-STD-001 Rev E requirement of holding a tip temp of +/-9F at rest? I am in a fight with an auditor over this. These irons do not require calibration but I need to know if they meet J-ST
Electronics Forum | Tue Jul 07 13:40:02 EDT 2020 | kierantennant
I have seen this calibration station. however do not understand how the next stage of calibration work. does the device calibrate the feeder itself or is it a manual process? IF so what is the process to get the feeder calibration correct?
Electronics Forum | Sun Jul 11 21:10:27 EDT 2010 | fujiphil
First, check the sensors for 17th and 19th station....tune the sensor amplifier if necessary. Then, check the dogs on the nozzle holders... If the above, items are ok... check the 13th station clutch engagement. Calibrate if necessary... fujiphil