Electronics Forum | Thu May 25 15:25:34 EDT 2006 | d0min0
hi, can't really see your picture, please rewiev the link regards Dominik
Electronics Forum | Thu May 25 15:50:05 EDT 2006 | Chunks
Given the magnification used on this picture, this does not look like a nodule I've ever seen.
Electronics Forum | Thu Jun 08 11:55:27 EDT 2006 | samir
Here's something funny: I named my new kitten, "Tin Whiskers."
Electronics Forum | Wed Apr 25 17:41:35 EDT 2007 | slthomas
A different perspective on tin whiskers altogether.
Electronics Forum | Sat Mar 21 06:56:09 EDT 2015 | robertwillis
Think you are talking about tin whiskers and not dendrites which are a different thing? Bob Willis
Electronics Forum | Tue Dec 13 10:27:46 EST 2005 | patrickbruneel
Samir, This growth doesn't look like a tin whisker which are needle like and very fragile (they don�t bend they break). I have seen similar growth in the past in an EMS defect analyses with connectors in stressed conditions. The growth seen was sim
Electronics Forum | Tue Mar 26 06:07:58 EDT 2019 | pooja_4t
Hi i am referring Tin whisker report JESD201A class 2 standard from Vishay. i can see at TC -55/85C using pbfree reflow there are 0 growth at 500&1000 cycles. for snpb reflow and the same temperature and same cycle significant growth can be found. my
Electronics Forum | Mon Mar 01 10:36:55 EST 2010 | patrickbruneel
Loco, Since Dave didn't respond i will. We shouldn't forget that even when using tin/lead solder the boards and components are still lead free. Parts that are not completely wetted by the tin/lead solder still have the potential for tin whiskering a
Electronics Forum | Tue Aug 17 17:06:43 EDT 2004 | davef
First, we'd like to see your supplier's minimum Sn thickness to be increased to 10um. Look here for support of this position: http://www.psma.com/HTML/FILES/forums/leadfree/hp_ext_pos_sn_for_pbfree.pdf Second, increasing the thickness of tin: * Ra
Electronics Forum | Fri May 19 09:34:56 EDT 2006 | Mark
I was wondering if anyone has the last 10 minutes of the Modern Marvels (Engineering Diasers 19) on a file they can send me? It talks and discusses the tin whiskers and problem with using tin.