Electronics Forum | Wed Oct 28 02:03:18 EST 1998 | Erhard Hofmann
| | | We currently using the Panasert SMT machine where PCB flow | | | direction were from right to left, & we are planning to move | | | in the FUJI -CP3 & CP4-2 in line where standard PCB | | | flow direction were left to right. | | | Any comment o
Electronics Forum | Wed Oct 14 16:58:30 EDT 1998 | Earl Moon
| It seems like most people want to X-Ray their BGAs. We're going to start doing a lot more of them and need to consider X-ray, too. | Q: Do most people/companies X-ray everyBGA or do they just do SPC? | Q: Can you get away with spending 25K? 30K? H
Electronics Forum | Wed Oct 14 13:52:59 EDT 1998 | Bill Schreiber
Dear Sanjay, An important issue involved when stencil printing adhesives vs. solder paste is: How do you clean the stencils after printing? Do you need two machines? Two chemistries? Two waste streams? What are the potential environmental impacts an
Electronics Forum | Tue Oct 13 18:28:51 EDT 1998 | Graham Naisbitt
Upinder, Using IPA does not cause the residue, it simply exposes it. Given that all fluxes leave reisdues, it follows that these MUST be benign - but how do you know, and how do you control it. You are using flux to remove oxides and give you a go
Electronics Forum | Thu Oct 15 13:55:43 EDT 1998 | Steve A
Dave, The first step would be to learn to accept the residue. IPC class 2 has no problem with it. If that is not possible, I am not sure why a no clean is necessary- but I will take your work for it. Alcohols will dry out the residue, and turn it
Electronics Forum | Thu Oct 15 16:39:07 EDT 1998 | Dave F
Steve: I thought Kyzen products were "additives" to either aqueous or semiaqueous inline or batch machine cleaning processes. I'm trying to clean the no-clean residue from a few components that can not bear to see water. Can you use Kyzen products
Electronics Forum | Sun Oct 11 00:23:26 EDT 1998 | MIKE
| Came a cross an interseting observation/question. | I'll need to filter additional information and specifics to those whom may be able to assist me. But for now; | | I use a water soluble base organic flux manufactured by Kester (the exact soluti
Electronics Forum | Mon Oct 12 20:51:14 EDT 1998 | Eric
| | Came a cross an interseting observation/question. | | I'll need to filter additional information and specifics to those whom may be able to assist me. But for now; | | | | I use a water soluble base organic flux manufactured by Kester (the exac
Electronics Forum | Thu Oct 08 03:33:50 EDT 1998 | Thomas Blesinger
| | I am trying to find out, what possibilities I have, to print solder paste on a board, when the task is to have 120 Microns thickness for the biggest part of the board (85% of the real estate), and then have 250 Microns of thickness on the remain
Electronics Forum | Wed Sep 30 10:38:42 EDT 1998 | Earl Moon
| Anyone have ideas how to get MIL 50884 Qualification?. | | We are a small/mid sized Flex, rigid-flex circuit shop in Canada considering MIL Qualification. Is there any web site that we could check out? | | any advice is appreciated. | thank