Electronics Forum | Wed Oct 01 10:30:33 EDT 2008 | stepheniii
Be sure to peel the potatoes. I saw a guy use a potato to purify gold on the TV show Rough Science. Seriously though I would think SAC305 to SN100C wouldn't be as bad as eutectic to leadfree.
Electronics Forum | Wed Apr 22 23:25:15 EDT 2009 | jandon
We were using AIM WS485 SAC305 and AIM NC257 SAC305 and we had problems with voiding and AIM�s narrow process windows. Now we are using Indium3.2 and Indium8.9 with much better results.
Electronics Forum | Sat Sep 12 10:12:20 EDT 2009 | tylaburg
My customer wants an SnPb 63/37 BGA soldered using SAC305 solder paste. What data is avaiable showing the long term reliability of the intermetallics of the solder joints?
Electronics Forum | Sat Sep 12 14:10:38 EDT 2009 | GSx
First, make sure that 63/37 BGA can withstand higher reflow temperature of of lead free SAC305 GSx
Electronics Forum | Mon Apr 16 11:10:13 EDT 2012 | kkay
We are thinking of switching over from sac305 to sn100. Has anyone had any experience with this changeover and is there any drawbacks to switching to sn100?
Electronics Forum | Tue Apr 17 13:42:06 EDT 2012 | gaz
I'd say it depends on the whole process you have. With our 5 zone oven, I could never get a profile that worked as well as SAC305, so we switched back.
Electronics Forum | Tue Apr 17 13:45:24 EDT 2012 | kkay
Actually we were looking into it for our selective solder process only. We are pretty happy with the results of 305 at smt.
Electronics Forum | Fri Apr 20 09:19:58 EDT 2012 | davef
kkay: I'm not real clear on where in the assembly process flow that you are considering replacing SAC305 with SN100. Please clarify
Electronics Forum | Fri Oct 01 01:25:55 EDT 2021 | sn
Thank you Djo for your sharing. By the way, do you know that which field/product will prefer to use SAC405 paste instead of SAC305 or lower Ag wt% alloy solder paste?
Electronics Forum | Tue Oct 05 12:46:02 EDT 2021 | emeto
From what I understand SAC305 and SAC405 are considered low silver content and have the better overall mechanical qualities compared to more silver or no silver.