Electronics Forum | Mon Aug 02 11:16:38 EDT 2010 | sdibuyer
Can anyone recommend a reputable / knowledgeable SMT expert in the Bay Area to work on a contract / consultant basis? 10-20 hours per week for 3 - 6 months. This person will assess solder joint health, drive DOEs to maximize results within existing c
Electronics Forum | Mon Oct 04 18:48:43 EDT 2010 | rsthompson
I am trying to assess current industry thinking on the question of whether or not lead-free BGAs (SAC or other) can or should be soldered in a tin/lead process. It seems there are differing opinions on this and I'm wondering what some of you are doin
Electronics Forum | Tue Oct 05 14:34:40 EDT 2010 | 18424
I am trying to assess current industry thinking > on the question of whether or not lead-free BGAs > (SAC or other) can or should be soldered in a > tin/lead process. It seems there are differing > opinions on this and I'm wondering what some of
Electronics Forum | Tue Oct 05 22:33:24 EDT 2010 | Mag10
Is there anyone performs solderability evaluation on PCB as a part of receiving acceptance criteria. It's costly to perform any form of physical evaluation whether simple as dip and look or wetting force balance. How do you have control in place to a
Electronics Forum | Wed Jul 06 09:27:49 EDT 2011 | rdouglass
Has anyone come across any good visuals for the solderability requirements for component leads with toe-down configuration? IPC-A-610 does not have any visual aids for this category and our inspectors are having a difficult time assessing based sole
Electronics Forum | Fri Mar 23 00:12:55 EDT 2012 | posinpcbfactory
J-STD-003B prescribes test methods, defect > definitions and illustrations for assessing the > solderability of printed board surface > conductors, attachment lands, and plated-through > holes utilizing either tin/lead or lead-free > solders. Th
Electronics Forum | Fri Feb 22 16:32:56 EST 2013 | davef
Jorge: I took this total posting to several fabs at IPC APEX. None was satisfied with the answers you receive from your supplier or the Forum members. They suggested that you get your board analyzed. They were surprised that your supplier didn't in
Electronics Forum | Fri Jan 16 10:05:37 EST 2015 | rgduval
Is anyone successfully and repeatably placing 0402 or 0201 components with an older GSM? We're looking at the possibility of quoting a new job with 0201's, and I need to assess the capabilities of the machine before I commit to the job. I've never
Electronics Forum | Mon Jun 05 18:45:07 EDT 2017 | zsoden
Hi Steve, I agree with your assessment, it would certainly seem like the pads are de-wetting. But what could be the cause of this? Contaminated solder? The boards are new out of vacuum sealed bags (with desiccant sachets), so I can't see it being the
Electronics Forum | Thu Dec 12 17:48:21 EST 2019 | davef
You proved that the standard solderability test of components may be effective for assessing aged components. Curious Minds Can you get the authorization to use a more aggressive flux? Will that flux solve the problem? What's it going to cost to qu