Electronics Forum | Thu Oct 26 17:48:47 EDT 2000 | Dave F
In response to your questions: 1) Suggestions on substrate material FR-4 or something better? Most PBGA are on BT. That might good for you, also. 2) Are there design guidelines for wire bonding pattern on the substrate? Several things: 1 Doesn�t
Electronics Forum | Sat Mar 15 20:24:13 EST 2003 | ramanandkini
Thanks Mr.Dave. Sorry for the delay. One of our major prolems in ENIG plated surface is that wire does not stick. For many years we were getting a bond strength of 14 grams in both ENIG and electroplated surfaces. Now one vendor supplies ENIG boards
Electronics Forum | Tue Jun 19 12:15:45 EDT 2001 | Gil Zweig
I have made reference to X-ray Ball Bond Signatures a number of times, and I cannot overstate the importance of quickly qualifying the overall ball bond pattern as either uniform in size and shape or not. Software is available that will make this qua
Electronics Forum | Thu Nov 26 03:59:50 EST 1998 | Chi-Ting Chen
I have some 1.25 mils Al wire bonding chip on board process. After epxoy-based encapsulation, I do some aging test. How can I "see" or prove that there is a "wire break" exist due to the tension of thermal cycling? How can I know the failure is cause
Electronics Forum | Thu Nov 26 06:07:40 EST 1998 | Earl Moon
| I have some 1.25 mils Al wire bonding chip on board process. After epxoy-based encapsulation, I do some aging test. How can I "see" or prove that there is a "wire break" exist due to the tension of thermal cycling? How can I know the failure is cau
Electronics Forum | Fri Nov 27 02:09:50 EST 1998 | Chi-Ting Chen
| | I have some 1.25 mils Al wire bonding chip on board process. After epxoy-based encapsulation, I do some aging test. How can I "see" or prove that there is a "wire break" exist due to the tension of thermal cycling? How can I know the failure is c
Electronics Forum | Fri Nov 27 02:11:17 EST 1998 | Chi-Ting Chen
| | I have some 1.25 mils Al wire bonding chip on board process. After epxoy-based encapsulation, I do some aging test. How can I "see" or prove that there is a "wire break" exist due to the tension of thermal cycling? How can I know the failure is c
Electronics Forum | Wed Jan 09 17:14:48 EST 2002 | mregalia
Do you bond with Al or gold wire? What happens if the Ni is over 150 microinches? Thickness of nickel is one those things that we have not been consistent with. The industry seems to pretty much universally call for 100-200 microinches. Our old board
Electronics Forum | Sun Mar 02 12:16:29 EST 2003 | ramanandkini
Recently, one of our new vendor supplied us PCBs with Electroplated Nickel and Gold. We have the other regular source giving us ENIG plating. In both the wirebonding quality is OK. How do we benchmark this? Which one is suitable for production with l
Electronics Forum | Wed Jun 25 06:43:06 EDT 2003 | cyber_wolf
We are currently producing a board for a customer that has about 400 gold fingers that get wire bonded after the assy. leaves our facility. We have tried many different approaches to ensure that we are not getting solder on the gold fingers. Nothing