Electronics Forum | Wed Jun 09 17:41:40 EDT 2004 | stevecrowley
Does anyone know of a 3rd party that manufactures the Mirae spindle? We have 5 broken nozzle spindles that need replacing. Also in need of renting or borrowing the Head Offset Jig so as when replacing said spindles we can measure the camera to nozzl
Electronics Forum | Fri Sep 10 14:25:07 EDT 2004 | Claude_Couture
We had the same problems a few years back. We complained and they came back with the excuse that the supplier of the parts had made a bad batch. They sent us a new part in exchange of the broken one. When faced with premature breakage of parts that a
Electronics Forum | Sun Dec 10 21:40:40 EST 2006 | villu
few days ago the camera picture started jumping like a TV between signals.. the blue Cable between the control board and the computer was Broken (last 3 threads) so we changed it.. but the problem is still there.. tested with another machines Compute
Electronics Forum | Wed Aug 13 19:57:05 EDT 2014 | suroy
After wash cycle, some of the inductors are open (broken wire). Resistance across the two ends should be below 4 ohms (normal) however on broken wire shows above 200 ohms. I am wondering if anyone else has seen this problem. We are using High-Reliabi
Electronics Forum | Mon Jan 05 16:07:21 EST 1998 | Terry Burnette
| | Hello all, | | I have experienced broken ceramic SMT parts. Most of the time, | | we have found fractured inductive beads. Once in awhile, we find | | broken Ceramic Caps. All parts we use are 1206 form factors and | | we use tape and reel...
Electronics Forum | Mon Dec 29 14:42:00 EST 1997 | justin medernach
| Hello all, | I have experienced broken ceramic SMT parts. Most of the time, | we have found fractured inductive beads. Once in awhile, we find | broken Ceramic Caps. All parts we use are 1206 form factors and | we use tape and reel... | Michael
Electronics Forum | Mon Dec 04 03:40:43 EST 2000 | jmlasserre
Hello, When we discover the broken caps, there are missing and we can observe only either the 2 terminaisons or a small part of ceramic. The defect is due to a shock during the process but it's possible that the caps are fragilized during an operati
Electronics Forum | Tue Mar 16 09:03:33 EST 1999 | Dave F
| Thanks Dave, | | But still I have the following question unanswered, in a technical point of view: | Has it sense to measure this on A system like we have now, because there are no wires that can be broken. | George: While I agree that no wires c
Electronics Forum | Wed Feb 05 11:38:46 EST 2003 | Stephen
Don't forget placement. I"ve seen chips broken when they are being placed because they were thicker than the parts data used for them. This is not an issue on Panasonic machines because they measure the thickness of parts but I have seen it happen
Electronics Forum | Mon Dec 26 13:24:12 EST 2005 | mariss
I'm assuming the fracture in tension; the fracture doesn't show even at X50. The broken edges are that clean. I would expect spalling at the fracture edges if it were a compression or torsional fracture. This makes me belive the board expands and pul