Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have
Electronics Forum | Fri Mar 24 11:12:06 EST 2006 | patrickbruneel
You�re a good man Rob and a good patriot, you defend your governments decisions even if they're wrong. Isn't the WEEE directive aimed at preventing electronics ending up in a landfill? This immediately takes away the leaching arguments and is a great
Electronics Forum | Mon Jun 20 10:59:18 EDT 2005 | Jason Fullerton
Extra cooling is better (Alpha recommends -3 to -7 degC/sec) for cosmetics. Less chance of s o called 'cooling lines' that look similar to 'cold' tin-lead joints. (Seems a bit steep to me - I worry about the risk of cracking ceramic caps.) Might be
Electronics Forum | Thu Sep 23 08:47:25 EDT 2021 | majdi4
1)Though in many cases the difference between SAC305 and SAC405 was small,and not always statistically significant, it was observed that SAC405 generally outperformed SAC305 joints. Under 0°C to 100°C thermal cycling,no statistically significant
Electronics Forum | Tue Jun 16 15:01:58 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Tue Jun 16 15:00:12 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Sat Mar 15 01:03:10 EDT 2008 | callckq
All, What if BGA solder crack do exist after the shock test? Its happen at the corner of the BGA. Base on your experience, what are the potential root causes? Thanks, Sean
Electronics Forum | Thu Mar 03 11:23:50 EST 2005 | Slow Ride
Generally QC is a different deptpartment than touch-up people. Most touch-up people are just general operators, so to keep their job they always see the solder joint as "not enough". Q.C. people are generally a bit better, but know they may be call