Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Mon Dec 16 19:05:57 EST 2002 | davidduke
Steve , I agree with all the responses you have received. Randy Villeneuve is absolutly correct in all of his assesments and I would consider him an expert with the process , Gris is correct about adding a "heat sink" to the process complicating pr
Electronics Forum | Thu Dec 05 11:04:27 EST 2002 | slthomas
They're IR, bottom side only. Frankly wave solder is not my forte (there are those that would claim nothing is), but I've personally been tasked with developing a process to do reliable, high volume bottom side SMT, so I'm drawing a lot from the tec
Electronics Forum | Fri Jul 13 09:27:15 EDT 2007 | losersk8er
Sorry I have just started working in this industry so I am not as familiar with everything. The probelm is with the Product shorting because of small pieces of metal stretching accross two leads of an IC. This could be a result of faulty equipment?
Electronics Forum | Wed May 27 13:42:08 EDT 1998 | Chrys
| R&D is currently designing a board with smt components on both sides of the board. They are adding a 16 pin IC Gull wing. on the bottom side of the board. I have asked for only caps and resistors to be placed on the bottom side. Is there a recommen
Electronics Forum | Thu Jan 24 13:23:53 EST 2002 | Shawn
Thank you all very much for the responses. The solder is eutectic and the problem, as far as I can tell, has been around before I was here, 2+ years. The flow machine is a treiber with 2 bottom preheaters and 1 top. The solder pot temp is 500F +/-4F
Electronics Forum | Fri Jul 13 11:33:54 EDT 2007 | realchunks
Just starting and already responsible for product quality and machine adjustment? Wow, you poor bastard. Ok, I will assume this problem happens on the bottom side of the board with a thru-hole IC. The short occurs on the side that doesn't have the
Electronics Forum | Fri Jul 13 16:45:37 EDT 2007 | losersk8er
The Contamination has proven to be pretty random, lots of stainless steel though in fact two cases in the past two days. As far as I know all machinery is cleaned regularly as well, even the stencil washer itself. The boards we make are 90% (at l
Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Tue Jan 31 12:13:26 EST 2006 | Calvin Kolokoy
Today's regular Sn-Pb paste chemistries are designed to run at higher peak temperatures ensuring that your lead-free alloys will coalesce with your regular Sn-Pb solder. That being said, it is do-able to solder both types in one oven. Generally, wit