Electronics Forum | Thu May 22 14:16:40 EDT 2003 | MikeF
We need more information to give you a good answer. Is this a leaded part (axial or radial) or smt? How big is the part, how much weight per lead? What is the end use environment, will it see any vibration? or temperature extremes? Some general com
Electronics Forum | Tue Apr 13 18:11:00 EDT 1999 | Jimmy Strain
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Apr 19 11:21:03 EDT 1999 | Travson
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Tue Aug 11 12:15:34 EDT 1998 | X-man
| | We need BGA rework station and x-ray inspector recently in urget case, Do you have any information to rework FPGA package and inspect them during processing. | Thx for any information | Best Regards, | Stoney Tsai Stoney, Probably the best rewor
Electronics Forum | Fri Jun 08 17:22:51 EDT 2007 | naynayno
We have been producing an IMS assembly with SMT dpak's for some time. However, we recently encountered a new problem by chance - the parts can be flicked off with a finger nail. I state by chance because the solder joints are wetted and shiny with
Electronics Forum | Thu May 23 13:24:14 EDT 2013 | rgduval
We agree that it looks like a touch-up process. However, we're not certain that it would meet Class 3 requirements. It appears to be an incomplete solder joint. The outer bit of solder shows voiding to the inside bit of the solder joint, and it lo
Electronics Forum | Tue Apr 13 18:39:24 EDT 1999 | Tom B
| | Netters, | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | 1. Kester 293 no clean | | 2. 2.1 C/s for 30s to 150 C | | 3. .5 - .7 C/s f
Electronics Forum | Tue Apr 13 23:08:56 EDT 1999 | Jeff Sanchez
| | | Netters, | | | | | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | | | | | 1. Kester 293 no clean | | | 2. 2.1 C/s for 30s to 150 C | | | 3.
Electronics Forum | Wed Apr 21 00:35:31 EDT 1999 | Scott Cook
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185