Electronics Forum | Fri Aug 26 14:15:16 EDT 2005 | David
Where could I find more information regarding the double sided reflow and flux problems with white tin?
Electronics Forum | Tue Sep 06 09:30:34 EDT 2005 | russ
I read it in Florida Cir-teks own literature. http://www.florida cirtek.com
Electronics Forum | Tue Dec 10 20:42:43 EST 2002 | davef
Vijay, Sounds like you're not spending enough time at liquidous plus 20*C. And you need to stay there for 5 to 10 seconds. I know, I know. We have used bucketsful of WS609 over the years. See, as you say, the melting point of your solder alloy
Electronics Forum | Fri May 31 08:51:09 EDT 2002 | zanolli
Hello Dave, As related to connector mating interface, fretting corrosion is the oxidation of the contact points, causing high resistance across the interface. Fretting corrosion is caused my micromotions in the interface exposing the metalized conta
Electronics Forum | Wed Feb 03 22:47:48 EST 1999 | Chris G.
| Hi! | | Does anyone know any roadmaps for board plating materials. Especially I'm interested in finishes, which are plated onto copper. | | Teemu M�kiniemi | Teemu, For some time now, as I am sure you are aware, the PCB industry has been tryi
Electronics Forum | Wed Aug 11 18:36:03 EDT 2004 | davef
90 Knoop. Q2: Thickness is 4 to 10 u" for Au and 300 to 400 u" for nickel A2: This looks like a ENIG spec. Although, the Ni is quite heavy, 150 uin is sufficient for most applications. [IPC-4552 ENIG specification: * Gold thickness of 0.075 - 0.125
Electronics Forum | Thu Aug 07 09:14:02 EDT 2003 | Carol
Thanks Dave, Much appreciated. Carol
Electronics Forum | Wed Aug 06 16:35:31 EDT 2003 | Carol
This is an old topic, but keeps coming up. Solderability and reliability issues with SMT gold plated terminations when used with tin/lead solder paste/hassle finish PWB. I need to know which standard (mil, IPC, J-STD??) tells you all about the probl
Electronics Forum | Fri Apr 13 22:38:19 EDT 2001 | edylc
Hi , Could you be seeing the nickel under the gold plating because you are removing some of the Gold with the Kapton Tape....?? You mean , the adhesive properties of the kapton tape will cause the gold plating on the gold finger to be somehow peel of
Electronics Forum | Tue May 14 22:09:04 EDT 2013 | ultimatejoker
Hi, what is significant different between PdNi and PdCo Plating? I found in some papers indicate that the deposit characteristics for both plating is totally the same.