Electronics Forum | Thu Jan 12 10:05:13 EST 2006 | davef
There's a lots comparisons like this on the web. Here's one: Westwood Associates said on 8/12/2003: ||HASL||OSP||ENIG||Pd||Tin||Silver Flat||no||yes||yes||yes||yes||yes Solderjoint||Cu-Sn||Cu-Sn||Ni-Sn||Ni-Sn||Cu-Sn||Cu-Sn Contact||E-test, ICT||no|
Electronics Forum | Wed Aug 31 12:33:25 EDT 2005 | Jaya
I have expirence running,double sided Imm gold boards recently which ed up a lot of solderability issue. The Imm gold need to be slightly more control during reflow oven area on it's profile.
Electronics Forum | Mon Jun 26 08:08:32 EDT 2006 | davef
It does make you think the immersion coating is causing the voiding, doesn't it? We never have seen that.
Electronics Forum | Tue Feb 19 16:19:26 EST 2008 | edatasys
Check out http://www.solderstar.co.uk/wavePro.html This tool measures all key wave solder information with a single pass. Wave/PCB contact, immersion depths, etc. Also has a reflow pack to allow use on reflow, 9 channels with predictive software. B
Electronics Forum | Thu Aug 03 10:53:23 EDT 2000 | Roni Haviv
Hello, Does enyone have any experience with Immersion Tin (Sn) as a finish process on PCB ? Any information will help ! Thanks Roni
Electronics Forum | Tue May 15 11:55:16 EDT 2001 | dason_c
We had a same problem before and Cirtech work with FAB supplier. It is due to the contamination on the tank. No special profile and paste use on the immersion tin board. Dason
Electronics Forum | Fri Oct 05 07:31:29 EDT 2001 | furrer
When tenting vias almost a few vias are not covered completly by Solder Mask. Does this one side open vias affect the Immersion Tin Process ? Do we get chemical residues in the vias ?
Electronics Forum | Mon Dec 31 05:07:59 EST 2001 | ronih
Hello, I need some information, even some initial information about Immersion Tin finish on PCB: solderability, environment sensitivity... Is this technology approved yet by anybody? Thanks Roni ORBOTECH
Electronics Forum | Thu Jan 11 08:52:17 EST 2007 | mattkehoe@sipad.com
Looking for a source to have an immersion tin finish evaluated for solderability?? Contact me direct 770-475-4576 Matt Kehoe
Electronics Forum | Wed Apr 04 19:25:58 EDT 2007 | TB
Dear All, anyone has experienced with thin layer of immersion tin (about 5 microns) on copper pads in term of long term reliability for first or second reliability studies. Any input will be greatly appriciated.. Thanks.