Electronics Forum | Fri Sep 17 15:01:05 EDT 1999 | Dave F
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Electronics Forum | Sat Sep 18 04:42:52 EDT 1999 | Brian
Dave, I'll respond by paragraph: | | | Brian: | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake burritos through
Electronics Forum | Sat Sep 18 12:27:21 EDT 1999 | Earl Moon
| | | Dave, I'll respond by paragraph: | | | | | Brian: | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slathered shiitake
Electronics Forum | Thu Sep 16 18:59:14 EDT 2004 | Carol
Thanks Everyone, the information was very useful. We use 7095 as a bible. A-610 6.5.3 doesn't allow for any solder balls not entrapped/attached etc. so we will look again at plugging/tenting both ends of the via. We ran into the problem of the mask
Electronics Forum | Tue Feb 01 14:21:24 EST 2000 | Dennis VanBuren
We are considering the use of Immersion Silver for a PCB surface finish. We currently use Immersion Gold surface finish, which has served us well. However, recent discussions on the cracking of corner joints on large pin count BGA packages, with the
Electronics Forum | Fri Dec 13 10:23:55 EST 2002 | davef
Bright ideas??? Bright ideas!!! I got bright ideas. In order of decreasing luminosity: * Stop installing the socket, solder the PLCC to the board, dip the board. The socket is a waste of time and money. You never replace the PLCC in the field, a
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Thu Jun 24 11:21:40 EDT 2010 | floydf
Hi, > > I have a 100nF 0805 ceramic cap (the most > common type!), Yageo brand (20+ pcs. on the > module). In our production run I get some errors > due to conductive caps (can be anything from 25 > Ohm to 5K - most are open of course). Only one
Electronics Forum | Tue Jun 07 16:19:58 EDT 2005 | davef
Q1) How to identify on good or bad ICs lead that could contribute to dewetting? A1) Distinguish between good or bad IC that could contribute to dewetting by testing for solderability, according to J-STD-002. Q2) What actions that must be taken in fa