A while back we checked out all our manufacturing equipment for lead free capability, we thought our soldering irons would all be fine as they can reach temperatures well in excess of lead free alloy melting points. Last week i was speaking to someo
Electronics Forum | Mon Jun 14 11:00:50 EDT 2004 | raylawre
This is one reason why we changed package styles. Maybe consider getting a different size tube, say from 500g to 1000g or something like that. We use jars for lead paste, and tubes for lead free (different application method) If lead free comes off t
Electronics Forum | Tue Oct 17 03:13:10 EDT 2006 | charless
Apoligies Steve if I did not explain myself clearly. We have made the same design using the same RoHs compliant components (which I am assured by the suppliers are process temperature capable) with both lead and lead free solder. Without wishing to
Electronics Forum | Tue Jul 12 11:26:38 EDT 2005 | jdengler
I think the asahi solder is coming out with their own irons if they get enough interest on this forum.
Electronics Forum | Wed Jul 13 03:35:18 EDT 2005 | Rob
.....and it'll probably be the best soldering iron in the world.
Electronics Forum | Wed Jul 13 15:14:48 EDT 2005 | jdumont
...Or how about the wireless wrist straps. Those are a lifesaver. Ok im done now.
Electronics Forum | Fri Oct 13 03:29:46 EDT 2006 | AR
Hi Could you specify what you mean by fracturing component legs?
Electronics Forum | Fri Dec 05 02:50:16 EST 2008 | lococost
So, no one is wave soldering 0603 succesfully? Not even teh wavemaster??
Electronics Forum | Thu May 11 18:59:40 EDT 2000 | lboone
Have anyone perform wave soldering on FR-2 and FR-1 printed circuit board with lead free soldering? Can you share the parameters(wave temperature,preheat temperature, contact time, wave height,etc,) used and did you do any changes to the wave solderi
Electronics Forum | Tue Jul 12 16:03:09 EDT 2005 | autoequip
I have recently been testing a new Iron that will be introduced on the market soon. The temp drop is coming in at 30c versus most other irons I have tested drop about 70c the tips are elctroplated and designed for lead free we have been very impresse