Electronics Forum | Thu Mar 10 13:05:41 EST 2005 | patrickbruneel
This phenomenon is caused by a high amount of halogens (Cl, Br etc.) used in the flux activators or in the flux surfactants. We've seen effects creating all colors of the rainbow. Changing to No-Clean (halide-free) will eliminate this color effect.
Electronics Forum | Mon Feb 18 13:11:41 EST 2008 | tonyamenson
Are there profilers that I can use over my leaded and lead-free wave that can also profile my reflow ovens (leaded and lead-free). I'm not that familiar with either but as I learn I can't help but think that there should be something on the market t
Electronics Forum | Tue Dec 13 09:29:08 EST 2011 | swag
We're soon to build a lead free assembly with 0201 components. I'm not worried about placement as our machines can handle it. Any tips on printing, screens, reflow?
Electronics Forum | Fri Dec 16 18:37:10 EST 2005 | mdemos1
Hi. I am trying to understand Tg and how it relates to reflow. With the higher temperatures of lead free, we have been looking toward laminates with a Tg of 180 instead of the current 140. My question is a little more general. In either lead free
Electronics Forum | Tue May 09 14:49:57 EDT 2006 | Larry
Hey guys, Anybody having trouble with increased false contact issues in ICT after switching from lead to lead free? Our test guys keep trying to imply that the flux residues are a problem (we're using Alpha EF2202), but as the soldering process eng
Electronics Forum | Wed May 10 00:46:32 EDT 2006 | Chris
I agree! I am using a SAC305 no clean from Alpha. I have noticed that even hand probing with volt meter leads requires me to press very hard on the pads to bust through the flux residue.
Electronics Forum | Tue Feb 19 07:44:41 EST 2008 | tonyamenson
So just to clarify.... If i bought a KIC 2000 I could run that one unit over both my waves and through both my ovens (leaded and lead-free)? Or would I need additional equipment to use it on the wave?
Electronics Forum | Fri Nov 12 09:19:07 EST 2004 | Dave G
Good places to start: http://www.nemi.org/ http://www.lead-free.com/ Dave G
Electronics Forum | Wed Dec 14 11:06:12 EST 2011 | swag
Thanks, Dave. Really good article.
Electronics Forum | Tue May 06 11:56:56 EDT 2008 | joeherz
We have a board that uses 0402x4 RNET packages that we are having a difficult time getting to solder consistently. Paste deposition is fine (using AIM WS353) and profile is dead-nuts. I'm starting to wonder if this is something that we're just goin