Electronics Forum | Wed Mar 04 22:57:05 EST 2009 | davef
Underfill epoxies may be classified into major groups [Capillary Underfill Manufacturing Development and Characterization for 2nd Level Electronic Interconnect Processes; B Salom�n; University of Puerto Rico, Mayaguez Campus; Dec 2004]: * Capillary.
Electronics Forum | Mon Jan 15 11:41:56 EST 2007 | davef
Questions are: * Does the component take solder when you dip it in the solder pot to test the solderability of the leads? * Can you get full barrel fill when wave soldering a bare board? * Is your flux reaching the top of the board through the hole b
Electronics Forum | Wed May 21 13:59:19 EDT 2008 | pjc
Here's what I've seen for no-clean flux applications: Leaded: Dwell Time is? 2 - 3 seconds Top side board temp max? If some small SMT parts reflow are we too hot? 110 to 120C top side board temp just before hitting the wave(s) Pot temp. 245C Lea
Electronics Forum | Thu Jul 13 13:52:28 EDT 2006 | George
Thanks Russ...
Electronics Forum | Wed Jul 12 18:25:23 EDT 2006 | George
Hi everybody: I really need your expertise on this one. I was told that the flux 270WR from AIM is either No-clean or WS soluble depending on your needs. I read the TDS and it looks like it is....but..... Is there anybody out there using this or s
Electronics Forum | Thu Oct 11 19:31:58 EDT 2007 | davef
We'd probably hand solder these coils with low residue fluxed wire solder, after cleaning.
Electronics Forum | Wed Jul 12 19:13:18 EDT 2006 | russ
i have heard of washable no-cleans for about 6-8 years now. I would think that if SIR values are acceptable for end use then I would run with it. Russ
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be
Electronics Forum | Mon Jan 15 09:19:29 EST 2007 | tk380514
We use Alpha EF-2202 low-VOC No-Clean flux Selective wave soldering cassettes Bottom pre-heating wave soldering machine We have one component that will not solder properly: http://www.epcos.com/web/generator/Web/Sections/ProductCatalog/Capacitors/Ul
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,