Electronics Forum | Wed Aug 30 09:56:37 EDT 2000 | NLykus
Hi Ramon, We have had this problem before on our Seho Wave Solder Machine. We are currently using a spray fluxer as well. By imersing the PCB into the flux you stated you are getting good results. What you need to do is check your spray patter
Electronics Forum | Thu Aug 31 14:27:23 EDT 2000 | Travis Slaughter
How to clean a contaminated board would depend on what it�s contaminated by, alcohol may be just the thing. If there is bare copper that has corroded that could be more of a problem, or maybe not if its due to poor tinning by the board house you coul
Electronics Forum | Tue Sep 21 13:10:10 EDT 1999 | Dave F
| Dear All, | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | I mean that I wonder why we use
Electronics Forum | Wed Sep 22 02:45:23 EDT 1999 | Brian
| | Dear All, | | | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | | | I mean that I wonder
Electronics Forum | Tue Jan 30 10:44:02 EST 2018 | emeto
If you go even further, the flux residue actually isolates the joints from the surrounding atmosphere, so it is actually supposed to be there. Adding a step in your process that is obsolete, doesn't comply very good with the whole lean concept. I don
Electronics Forum | Thu Feb 01 15:36:42 EST 2018 | davef
Not to be repetitious, I just don't remember if this has been said or not, I'm old, give me a break. Some people have found that DI water is too thick to properly remove flux residue under low stand-off components.
Electronics Forum | Tue Jan 30 07:29:21 EST 2018 | charliedci
I believe the correct statement (I've been told) is "the process is no clean". The solder paste is "low residue". As a CM, in the past we had customers that insisted on a wash after soldering. We used DI water with a saponifier which had mixed result
Electronics Forum | Sat Mar 27 12:36:34 EST 1999 | Scott Cook
| Hi, | I have a customer who's electronic assemblies produce RF. He is insisting upon aqueuos cleaning. We switched to a no clean solder years ago and no longer have an aqueous system. | Is aqueous cleaning necessary to eliminate 'cross talk' of
Electronics Forum | Thu Apr 01 09:10:55 EST 2004 | cyclopsn
We are currently using non clean paste and non clean flux in our manufacturing process. But recently our customer feedback that using a non clean process might cause flux blockage in via hole area and potentially might burn or explode the boards over
Electronics Forum | Wed Jul 08 07:01:16 EDT 2009 | Jeff
We use Kester 979 no clean flux in our Ersa.