| | | Hi all, | | | | | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | | | | | We are producing VGA cards and mother boards for PC's all components to be wave so
Electronics Forum | Tue Sep 21 07:47:31 EDT 1999 | Wolfgang Busko
| | Hi all, | | | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are
Electronics Forum | Mon Jun 09 03:03:26 EDT 2003 | iman
With mounting interest in the "Automated Optical Inspection" thread revolving around SMTnet, was wondering from a end-user point of view, does anyone have recommended configuration AOI machine to recomend for purchase? what were the key benefits o
Electronics Forum | Fri May 31 12:50:42 EDT 2013 | spoiltforchoice
Is this a "thermal balance" issue? In the 2nd image you have a group of pads blobbed together as one giant pad. IMHO this is a bad idea, QFN's rely heavily on the magic of your paste and good PCB design to get good alignment. When your solder paste i
Electronics Forum | Mon Sep 20 09:02:34 EDT 1999 | Wolfgang Busko
| Hi all, | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are TH, the S
Electronics Forum | Mon Jul 08 03:09:12 EDT 2002 | Benny
Hi all How can I find the technical paper or source of information about using No-clean flux with high frequency apllication. High frequency mean more than 2 GHz - 5 GHz. I heard from my colleague that No-clean flux residue on board effect to high
Electronics Forum | Thu Aug 28 09:30:20 EDT 2008 | patrickbruneel
Omid, No-clean fluxes need to be used right out of the can without thinning. In the past with RA and RMA fluxes you could adjust or thin them to your desired density because they had plenty of solids up to 30%. No-Clean fluxes have a lot lower solid
Electronics Forum | Thu Aug 28 16:03:08 EDT 2008 | wavemasterlarry
I guess you're adding the gas to keep the fingers clean - sounds likeyou got your threads mixed up on the Forum. Any way I would suggest not doing this. Gas is pretty flammable. I have pix of one our Hollis cleaning machines going up in flames cau
Electronics Forum | Fri May 31 18:00:55 EDT 2013 | hegemon
With regards to first picture.(Large themal vias) I would attempt to measure the area of the ground pad, less the area of the "drain" holes or Thermal Vias. From that result I would reduce the aperture to account for about 50% coverage of that remai
Electronics Forum | Wed Jul 16 18:08:11 EDT 2003 | mgershenson
OK, disclaimer; I'm a salesguy, but I was a process engineer for quite a lot longer than I've been in sales. Your question is very vague, and may be difficult to answer. There are many ways to configure AOI to inspect solder, but as has been pointed