Electronics Forum | Tue Feb 01 09:53:37 EST 2005 | Howard Sommerfeld
I also have a spreadsheet tool for comparative analysis using criterion weighted scoring. It can be used to analyze any decision, and helps groups reach consensus on why a particular alternative is the way to go. As final steps you can also consider
Electronics Forum | Mon Feb 07 13:20:03 EST 2000 | Dave F
Graham STOP!!! You can not be totally serious. A five year old cost model counts bean, and beans are beans. I have to know more about the calculation. If this bores some of your gear-heads, click on "return." � Help me with the terms: - "Ops cos
Electronics Forum | Fri Jan 28 12:29:01 EST 2005 | Bob R.
We use the exact same method Chunks outlined for evaluating just about anything we're going to roll out worldwide, whether it's a material or a machine. List your factors (print speed, solder spread, etc), assign each a weight, evaluate each paste a
Electronics Forum | Tue Aug 30 15:05:23 EDT 2005 | Shean Dalton
Dear Ing, Have you analyzed why some RF device aren't operational after washing? An assumption is that failures are related to the ultrasonic energy applied. Other possibilities are for poor rinsing, poor drying, inadequate washing on those failed
Electronics Forum | Fri Jan 28 12:18:32 EST 2005 | Chunks
Your best bet is to do a decision making matrix. Each company has so many different criteria�s it's hard to pick out which one might be important to yours. Simply pick out your top 5 paste manufactures. Next decide what your "Eliminators" are - th
Electronics Forum | Tue Nov 14 22:01:07 EST 2000 | Dave F
I'd love to get to the point that I could discuss the impact of flux on dross formation. Until then, I fight with proper solder pot temperature, maintaining enough pump speed, and solder contaminants.
Electronics Forum | Mon Sep 18 19:58:10 EDT 2000 | Dave F
broad answer. There's tons of suppliers. Go to "Circuit Assembly" magazine web site and look-up flux suppliers in the "Buyers Guide." Broad line suppliers are Kester, Alpha ... They will make you answer: I'm joining bla, bla, bla metals, using b
Electronics Forum | Tue Nov 21 22:15:59 EST 2000 | Vince Whipple
Mohammed, The first suggested place to start with your question would probably be with your flux Mfr. Push them! The quantity of dross is effected by several factors: The higher your solder pot temp., the higher your dross level... but don't go too
Electronics Forum | Wed Jul 31 07:51:31 EDT 2019 | ameenullakhan
Hi Dave, lead is 80Pb/20Sn. Top joint off CCGA lead is SN63/Pb37. Thermocouple was placed at center lead of the CCGA and one at the corner lead of CCGA. Ramp Rate Center 1.09 Corner 1.26 Soak ( 140 - 160 deg C ) Center 37sec Corner 38sec Ref
Electronics Forum | Wed Sep 16 03:17:47 EDT 2009 | geb
The solder wire uses a ORL0 flux. The wire contains less flux at around 2.0-4.0%.