Electronics Forum | Thu Oct 02 17:00:44 EDT 2008 | davef
Is that accurate? If so, what are your aspect & area ratios? [Similar to the JerryS comment above.] * You say, � � and the average height is very high: nearly 200 pct.� => Our troop can make paste that height too. They snap the stencil-off a fast as
Electronics Forum | Tue Nov 09 17:12:38 EST 1999 | Dave F
Steve: Addressing your points: 1 FINE PITCH APERTURES Electropolishing Laser Cut Stencils: Laser cut should not requiring polishing. Geesh, how much money do you have for stencils? ;-) Oval Shaped Apertures: Pass. What do you expect to gain f
Electronics Forum | Tue Jun 01 19:23:15 EDT 2004 | Ken
profile it for the tin/lead paste. The tin in the solder paste will begin to disolve the sac ball. This is exactly the same scenario as 90/10 (80/20)high temp balls found on ceramic bga and many super bga devices (except the sac balls are now tin r
Electronics Forum | Thu Oct 02 12:22:26 EDT 2008 | JerryS
Hello Ok there is not much info here. What you have to mae sure of is several key factors. 1. Have you entered the correct stencil thickness. 2. Are you using the stencil gerber (not the paste layer) The paste layer is usually not adjusted for ap
Electronics Forum | Thu May 06 06:47:12 EDT 2004 | praveen
Hi, I just need to undestand any issue? If I mount Pb free BGA and use normal SN/Pb solder paste?
Electronics Forum | Steve Thomas |
Sat Nov 13 15:18:11 EST 1999
Electronics Forum | Wed Jun 02 19:01:50 EDT 2004 | lynnmc
Thanks to all on this feedback
Electronics Forum | Fri Oct 01 01:27:58 EDT 2021 | sn
Hi Davef, thank you for your information.
Electronics Forum | Fri Oct 01 03:16:39 EDT 2021 | sn
thank you for your information.
Electronics Forum | Mon Nov 14 10:10:52 EST 2005 | davef
When soldering your full tin (no lead) and Pb95/Sn5 solder components, you need to modify your PbSn reflow recipe to compensate for the higher melting point of the changed solder alloy [with your Sn62/Pb36/Ag2 solder paste] on those component leads.