Electronics Forum | Tue Feb 01 11:54:14 EST 2005 | TomA
Indy, I found the same findings as you. The claim is that the solder joint may actually look closer to a SnPb solder joint then the SAC alloys. I had commited to the SAC alloys at SMT before finding out about the SN100C alloy. I'm interested in what
Electronics Forum | Thu Dec 22 12:05:37 EST 2005 | Tony
Currently we are using a 2 step vapor soldering process to manufacture our std. lead soldered parts. The first step was done with a ls240 vapor fluid and the second was done with a ls200 fluid. Using a 221 deg C sn95/Ag5 solder for the first step a
Electronics Forum | Wed Sep 07 17:04:28 EDT 2005 | bhu
Anyone have any recommendations for hot air, hand held rework stations? We currently use Hakko for leaded assembly. We already have a sniper for bga rework.
Electronics Forum | Mon Jan 31 16:59:22 EST 2005 | frankracine
Hi Jay, Concerning you PCB, what TG do you expect to use for your lead free process? On my side I have a problem. I order PCB from Canada and from China. My PCB vendor in china is producing a lot of OSP and ENIG PCB, no HASL lead free and in Cana
Electronics Forum | Sun Feb 27 17:06:18 EST 2005 | Darby
This is the profile we came up with on a 1500 to satisfy the parameters suggested by Indium. This was on an FR4 1mm thick 4 layer pcb that I would descrbe as medium density, QFP, SOP, AL-CAP, TANTS, D-PAK, MINI SPRING COIL, SOT and CHIPS were all use
Electronics Forum | Wed Aug 31 06:33:04 EDT 2005 | Slaine
if a solder has over 85% lead its classed as RoHS complient because its difficult to achive the same melting point with anything else (298degrees). a few other alloys with a similar range are ; % % 266E266 82.6 Cd 17.4 Zn 271MP 100 Bi 280E2
Electronics Forum | Thu Jan 27 16:43:15 EST 2005 | russ
Ther is a solder alloy out there that is supposed to allow lead free wave processing without having to upgrade pumps and such or increasing the pot temp (direct drop in). I have not used it nor do I plan on doing leadfree wave soldering but you may
Electronics Forum | Sun Nov 27 20:47:51 EST 2005 | lerry king
such as : 1, Proof of Design (POD) The DFM/CE Book for Printed Circuit Boards, Assemblies and All Manner of Other Things Technical - by Earl Moon 2, Surface-Mount Technology for PC Boards James Holloman PROMPT Publications July 1995 509 pages 3,
Electronics Forum | Mon Jan 25 13:42:35 EST 2010 | patrickbruneel
This is a post from another forum as a response from Bob Landman to a claim that he had no evidence to be concerned about lead-free in hirel applications (interesting read). See below and am sure many technetters will find this interesting **********
Electronics Forum | Thu Jun 07 03:54:16 EDT 2007 | testbloke
I currently have issues with "slivers" of solder on or behind QFP devices. This has only occured on PB Free boards (we currently produce PB and PB Free on same equipment). This is not tin slivers, this is a long thin sliver of solder measuring up to