Electronics Forum | Mon Nov 27 17:47:23 EST 2000 | Dave F
Gyver: Lemme take a wack [if you�ll excuse the expression, given direction of the later discussion] at your questions. Q1. Will the baking of BGA or PCB cause more oxidation before the SMT process? A1. It certainly will not cause less oxidation,
Electronics Forum | Wed Aug 01 09:36:17 EDT 2001 | Pete Barton
Jay, > > I agree with your assement and Chips on > the Quads. I once worked at a shop that had Quads > and DynaPerts(at the time) The perts were > slower(TIME) and required(EFFORT/PEOPLE) more > MAINTENANCE(more effort more people and more > re
Electronics Forum | Fri Aug 02 12:01:40 EDT 2002 | johnw
interesting, not at all what we were told so yes lot's of contradictions comming from them, I have to say personally I've not beein impressed with there technical service of late, are they getting complacent I ask? it's strange they say it'll cause
Electronics Forum | Thu Jan 21 19:38:24 EST 1999 | dean
| Hello, | | I will be evaluating and qualifying two equipment types. The first is a fountain soldering device. I need practical advice on all the stuff you guys and gals know about as good, bad, ugly, best applications, setup, limitations, and all
Electronics Forum | Thu Jan 21 20:22:02 EST 1999 | Earl Moon
| | Hello, | | | | I will be evaluating and qualifying two equipment types. The first is a fountain soldering device. I need practical advice on all the stuff you guys and gals know about as good, bad, ugly, best applications, setup, limitations, an
Electronics Forum | Wed Dec 26 14:21:47 EST 2007 | gersla
I am looking for suggestion of BGA 0.5mm pitch Ball 0.3mm (BGA 8x8mm)assembly and soldering. Stencil thickness? Stencil reduce? Etc.
Electronics Forum | Tue Jun 01 19:23:15 EDT 2004 | Ken
profile it for the tin/lead paste. The tin in the solder paste will begin to disolve the sac ball. This is exactly the same scenario as 90/10 (80/20)high temp balls found on ceramic bga and many super bga devices (except the sac balls are now tin r
Electronics Forum | Thu Dec 27 11:05:40 EST 2007 | realchunks
5 or 6 mil thicjk stencil and no reduction.
Electronics Forum | Fri Dec 28 17:02:04 EST 2007 | davef
We agree with Chunks
Electronics Forum | Tue Jun 01 19:25:19 EDT 2004 | Ken
...oops part 2: I will assume a sac 350 ball??? 217-218C this will completely reflow the ball and form a "normalized" joint with a collapsed structure.