Electronics Forum | Sun Nov 08 15:27:25 EST 2015 | davef
Thinner: Flux thinner, NOT paint thinner We kept a spare stone in thinner in inventory. We cut PVC pipe to size, cap in one end, screw thread on the other, stone inside, filled with flux thinner and covered with a screw cap. I don't remember who we
Electronics Forum | Tue Feb 23 16:45:36 EST 2010 | dyoungquist
Davef is right on as usual. We are doing exactly what you do. Some smt with no clean paste then the plate through connectors on our selective solder machine using water soluble flux. We then clean with a ultrasonic water process. We do see the re
Electronics Forum | Fri May 14 09:00:35 EDT 2010 | rafacadiz
I attached a RX picture. A lot of voids and micro balls arround the flux residue. What do you think, relow temperature reflow or OSP poor weeting.? I appreciate your comments. Thanks,
Electronics Forum | Wed Aug 21 13:28:20 EDT 2019 | ameenullakhan
And what is the solder paste selection recommendation for the same. 1. Water soluble ( organic based flux solder based ) 2. No clean ( rosin or resin based solder paste ) customer is suggesting water soluble chemistry , which is having lot hot an
Electronics Forum | Fri Apr 15 11:15:14 EDT 2011 | wrongway
Hello all lets see you are wanting to place 60,000 parts a day make sure you derate the machines you are looking at to about half of what they claim and your change over will take some time as well we do several change overs each day up to six tim
Electronics Forum | Mon Apr 18 10:07:19 EDT 2011 | wrongway
Hello Jebs we started out that way but the more handaling of the pcb the more problems you will have if you can do it in line and have the pcb's stop at some of the conveyors you can do some inspection. yes all of our machine's are in line now we lo
Electronics Forum | Tue Dec 04 09:48:43 EST 2001 | davef
Defining the thickness of solder between the lead and the pad, J-001 states "Properly wetted fillet shall be evident." J-001 is available from http://www.ipc.org. Factors that affect this are: * Amount and composition of solder * Amount and compo
Electronics Forum | Mon Apr 26 09:46:05 EDT 1999 | C.K.
Chrys: I have checked all the basic elements of Wave solder joint formation: fluxing, preheating, and lastly soldering. For checking the fluxer, i used a product from ECD that's very similar to what you desribed called the flux-o-meter. It did a
Electronics Forum | Thu Jul 12 16:14:20 EDT 2007 | realchunks
Hi Scott, Hard to tell what kind of problem you really have. I guess you need to describe your process first. What kind of process are you using. Wave solder, reflow solder, etc.. What kind of flux are you using to solder with? Vaccum? What ar
Electronics Forum | Sun Apr 25 12:05:50 EDT 1999 | Chrys Shea
| | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free solderin