Electronics Forum | Wed Aug 21 13:28:20 EDT 2019 | ameenullakhan
And what is the solder paste selection recommendation for the same. 1. Water soluble ( organic based flux solder based ) 2. No clean ( rosin or resin based solder paste ) customer is suggesting water soluble chemistry , which is having lot hot an
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Mon Apr 09 20:55:46 EDT 2012 | action_101
I forgot to add that we are using a 3 mil stencil. It seems like to me that may be there isn't enough flux left when we reach liquidous?? About half of the solder spheres do melt and wet on each pad, but the top half of each solder joint is just the
Electronics Forum | Wed May 03 20:24:22 EDT 2000 | Dave F
MF: I know of nothing that addresses your question directly. Let me suggest: * Technical types at your solder supplier should be able to help. * "Effect Of Intermetallic Compounds On The Thermal Fatigue Of Surface Mount Solder Joints" PL Tu, et a
Electronics Forum | Thu Jun 27 11:22:03 EDT 2002 | robbied
Hi there. We have had an out of control reflow oven that has allowed its temperature to fluctuate by up to +/- 20 deg C from set point in very short periods of time. We found the root cause of the problem and fixed it, but by then we had already run
Electronics Forum | Tue Jan 16 07:07:17 EST 2007 | tk380514
Answers: The component does take solder, no problem We get a full barrel fill with an empty PCB but only on one of the holes, the other hole has so much copper around it. The flux reached the top of the PCB when I tested the empty PCB. The IPC-A-610
Electronics Forum | Mon Apr 09 19:50:33 EDT 2012 | action_101
Hello, We're building some boards with 01005's and the only issue we are running into is the solder is not reflowing. It's the damnest thing, we are having no issues with the printing process or placing the components, the two areas we thought we wo
Electronics Forum | Tue Nov 06 22:37:35 EST 2012 | davef
Ryan ... "As for bismuth-based lead-free alloys, a lower melting temperature than that of tin-lead is offered together with a cost similar to that of tin [in the area of $3/lb]. Unfortunately, bismuth in soldering alloys tends to create embrittlemen
Electronics Forum | Thu May 13 09:52:34 EDT 2021 | winston_one
Want to update this question a little, I know it appears few years ago, but I hope there is some updates... We have to assembly few samples of motherboards with this kind of finish (customer mistake during pcb order). Normally we can use leaded sold
Electronics Forum | Mon Jun 08 14:19:30 EDT 1998 | Gary Simbulan
Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have