Electronics Forum | Mon Jun 30 08:55:31 EDT 2008 | davef
It will be tough to find a dimensional thickness specification for HASL. IPC-6012 Table 3-2, line "Fused tin-lead or solder coat - Coverage and Solderable" states the requirement that there has to be complete coverage of solder on the land, and it mu
Electronics Forum | Sun Jun 29 15:03:04 EDT 2008 | jensteele
I was referring to the HASL supplied by the supplier...specifically Lead Free HASL. I've been searching the web and I cannot find a thickness specification like we have for ENIG and Immersion Silver.
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so
Electronics Forum | Fri Mar 03 09:48:06 EST 2000 | Wolfgang Busko
I have heard about it. The main reason is to save money. The problem is, or better is said, that the mixing isn�t that simple for you got have a homogen paste afterwards and the solderballs shouldn�t be deformed in size so that problems during printi
Electronics Forum | Fri Mar 03 09:48:06 EST 2000 | Wolfgang Busko
I have heard about it. The main reason is to save money. The problem is, or better is said, that the mixing isn�t that simple for you got have a homogen paste afterwards and the solderballs shouldn�t be deformed in size so that problems during printi
Electronics Forum | Tue Oct 12 13:03:18 EDT 2021 | cunningham
Afternoon all, Do you use any special surface other that ESD matting when changing over matrix trays? We currently use a earthed wire trolley that we keep trays and MSD bags on and when replenishing stock its carried out on the trolley. Does anyon
Electronics Forum | Thu Sep 23 08:08:12 EDT 2021 | SN
Hi. Anyone in this forum experienced the lead-free solder paste SAC305 and SAC405? What are the differences to expect for solder paste with SAC305 and SAC405? What is the effect of silver (Ag) alloy in solder paste? It was really appreciated if could
Electronics Forum | Mon Apr 16 18:49:40 EDT 2012 | tris101
Hi guys, I'm looking for some tooling parts and I hope you can point me in the right direction. We design basic in house reflow Carriers to surport boards during reflow. I would like to add clamps to our designs but I can not locate any off the she
Electronics Forum | Mon Apr 17 19:42:34 EDT 2000 | Russ Cutler
We just bought a new Heller 1800 EXL reflow oven for reflowing SMT boards. We us a low temp RMA solder paste with 2% silver. Everything we build is to IPC Class 3 specifications. We have approximately 600 different types of circuit boards we build
Electronics Forum | Mon May 13 11:17:57 EDT 2002 | genny
I think for our company, the reason we have not yet tried it is two fold. One - we are just barely starting to see a need on a new product under design for a flat finish, so currently we don't use any of the really flat finishes available. Two - Silv