Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Thu Nov 21 11:19:58 EST 2013 | davef
Generally, solder connections and leads are conformal coated, unless there is a reason not to coat them.
Electronics Forum | Tue May 23 15:40:17 EDT 2000 | larry
We currently use both Humiseal and Conap with OA flux. The flux MUST me cleaned off the assembly before coating. I know that Humiseal has coatings that are compatiable with no cleans as long as your processes are defined properly before your coating
Electronics Forum | Tue Aug 30 12:08:09 EDT 2005 | slthomas
The answer for us at my previous employer was water soluble flux. Wash the board, no residue. If you're not set up to wash (needing a washer, DI water source, waste treatment, ventilation, etc.) it can be expensive and space consuming. Do some resea
Electronics Forum | Mon Oct 03 12:11:18 EDT 2005 | PWH
Soon we will be manufacturing board assemblies on our SMT lines that will utilize both lead and lead free water soluable solder pastes. I have read some discussion about change-over from lead to lead-free jobs related to machine cleanliness, etc. H
Electronics Forum | Tue Aug 30 15:05:23 EDT 2005 | Shean Dalton
Dear Ing, Have you analyzed why some RF device aren't operational after washing? An assumption is that failures are related to the ultrasonic energy applied. Other possibilities are for poor rinsing, poor drying, inadequate washing on those failed
Electronics Forum | Fri Jan 26 13:26:30 EST 2007 | rw
We are developing a new product that requires conformal coating on the motor controller. We selected a silicone based conformal coat due to its ease of use. There has been disagreement among engineers as to its impact on the motor. We have contact
Electronics Forum | Wed Nov 20 16:47:10 EST 2013 | aaronpavone
I have a right angle male shrouded connector and the whole set of termination leads is tin lead plated, at least 100 microinches thick. Should the entirety of the lead be conformal coated? Or can we have just the joint coated? I know I have coated le
Electronics Forum | Tue Feb 23 16:45:36 EST 2010 | dyoungquist
Davef is right on as usual. We are doing exactly what you do. Some smt with no clean paste then the plate through connectors on our selective solder machine using water soluble flux. We then clean with a ultrasonic water process. We do see the re