Electronics Forum | Mon Dec 17 15:41:15 EST 2007 | shrek
Ha-ha-ha-ha-ha,me lad. Wave solder is like an onion, it's got many many layers. Kind of like me-self. I'm a big ogre with many complex layers. At any rate i like the other colleague with his adverstising trigger finger. by golly, me chap, he's a
Electronics Forum | Mon Dec 17 14:16:44 EST 2007 | realchunks
This is funny. Poeple giving answers to a question that isn't specific. What if the shorts he is having are on the top of his board, caused by flooding or Omega wave too high?
Electronics Forum | Mon Dec 17 02:08:21 EST 2007 | mun4o
Hi, I have a lot of solder bridge in our wave soldering process.We use SACX0307 and Surf 11 flux.the SW mashine is Vitronics delta 6622.Itry to change flux and termoprofile but results is not god.Can you halp me - recommend me some flux or other adv
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Fri Apr 20 16:05:17 EDT 2001 | gcs
We always reduce side to side, EXAMPLE: 12 mil width reduced to .010". Do you guys check viscosity ? Also maybe your guys are appling to much pressure on the sqweegee blades.
Electronics Forum | Sat Jan 29 05:43:51 EST 2005 | Chua
Hi Chunks, Thanks for your input. Appreciate you could send me a copy of your evaluation list as this type of evaluation is new to me..... Here is my email address :- pgchua@cyberway.com.sg Thanks.
Electronics Forum | Tue Feb 01 20:08:39 EST 2005 | davef
Look here: http://www.epa.gov/ozone/snap/icel/noclean2.pdf
Electronics Forum | Fri Jan 28 12:29:01 EST 2005 | Bob R.
We use the exact same method Chunks outlined for evaluating just about anything we're going to roll out worldwide, whether it's a material or a machine. List your factors (print speed, solder spread, etc), assign each a weight, evaluate each paste a
Electronics Forum | Fri Apr 20 11:05:23 EDT 2001 | gcs
Just a bullet! My results are, .005" stencil thickness should measure between .0055" - .006" if your pressure is correct, metal blades and snap-off is set up correctly. Do you have aperture reductions at the QFP locations "typicial industry standard