Electronics Forum | Sun Mar 15 23:58:01 EST 1998 | Phill Hunter
| | I am having a problem with Entek coated boards. The solder past seem to just ball up on the pads. I had no problems with the board when it was hot air leveled. The board is double sided surface mount. I have tried adjusting the oven profiles m
Electronics Forum | Thu Jan 08 15:03:40 EST 2004 | dwzeek
We have an ongoing problem with our QFP144 packages soldering. It has not received much attention until late due to some customer failures. Most of the failures would show up in ESS testing and be repaired. The failure rate is about 2 in 1000 parts f
Electronics Forum | Mon Jan 21 19:22:38 EST 2008 | davef
In your situation, the issue is the compatibility of your flux residues and the encapsulant that you choose. First, contact your encapsulant supplier for advice. They've likely been down this road with other customers and may be able so save you som
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 10:15:34 EDT 1999 | Vic Lau
| | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a dou
Electronics Forum | Mon May 31 21:50:59 EDT 1999 | Dave F
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Thu Jan 08 16:16:09 EST 2004 | Dean
My first concern would be the choice of solder paste you have. There are better chemistries out there that far exceed the capabilities of the 609 2. Yes, the part will partially float on the solder (assuming plastic qfp). Cross sectioning would sho
Electronics Forum | Thu Jul 15 18:07:04 EDT 2004 | dwanzek
This has been a tough one to date. Any ideas will help. Problem definition � random QFP144 part not soldering all leads. Percentage fallout is about 1-5% of boards. Usually leads, one or more, on trailing side to the direction of travel does not wet
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Thu Apr 16 13:50:49 EDT 1998 | Lou
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X