Electronics Forum | Tue May 09 18:00:33 EDT 2006 | russ
in all actuality, you are both right. Alpha metals does have the toughest/hardest noclean residue that I have seen. When changing to no-clean FLUX you should run different probes. So back to square one. You're both right so who's gonna win?
Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir
Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll
Electronics Forum | Fri Feb 04 09:23:21 EST 2000 | Casimir Budzinski
If No-Clean flux does not need to be cleaned, then why do I get readings of up to 27(ug NaCl/sq in) on boards that are not washed, up to 23.4(ug NaCl/sq in) on boards washed with DI water only and from 1.2 to 10.1(ug NaCl/sq in) on boards washed with
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Tue Feb 29 10:14:02 EST 2000 | Robert Hartmann
My company is just getting into the flip chip packaging arena. We are putting in a prototype/small volume wire bond PBGA line. We have some questions with regard to choosing solder balls and cleaning of flux. 1) Is there a formula for the shrink
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Mon Apr 26 17:31:14 EDT 1999 | Earl Moon
| Hey MoonMan, | | Did I catch in one of your fabulous threads that you're using Tetra stencils? I'm anxious to find out how you're liking them. | | We we're all set up to go to Tetras, then mgt decided to close down our factory - Dooop! "Foiled"
Electronics Forum | Tue Apr 27 05:26:14 EDT 1999 | Charles Stringer
| | Hey MoonMan, | | | | Did I catch in one of your fabulous threads that you're using Tetra stencils? I'm anxious to find out how you're liking them. | | | | We we're all set up to go to Tetras, then mgt decided to close down our factory - Dooop!
Electronics Forum | Tue Apr 27 09:26:43 EDT 1999 | Chrys Shea
| | | Hey MoonMan, | | | | | | Did I catch in one of your fabulous threads that you're using Tetra stencils? I'm anxious to find out how you're liking them. | | | | | | We we're all set up to go to Tetras, then mgt decided to close down our factor
Electronics Forum | Wed May 20 07:13:15 EDT 1998 | smd
Does anyone use the "Quick Frame" with their Dek printer? The threads on the screws keep stripping, so we thought maybe we'd send our frames to a machine shop for heftier screws. Has anyone done this? Is there a better way? Isn't it weird how Alpha k