First, let me say what I always say: a good chem-etched stencil will print fine pitch. Chem-etch brings trap to the side walls because its a physical by-product of the process. Because they are less expensive you can add electropolish and still save
Electronics Forum | Thu Sep 05 23:18:03 EDT 2013 | feiyangniao
There is a new toy I received today: a NeoDen TM-240A automatic desktop pick and place machine! I’ve kept my eyes on this baby for a quite a while, and finally decided to make a purchase last week. The shipping was very fast: DHL from China, a total
Electronics Forum | Tue Nov 28 21:16:17 EST 2006 | davef
J Rose at EMPF says: The introduction of no-clean solder fluxes in electronics manufacturing has given rise to greater levels of solder balling simply because the opportunity to remove them in the wash process does not exist. They are typically cause
Electronics Forum | Tue Oct 12 10:24:50 EDT 1999 | Jose RG
Hi, We are in the way to evaluate different solder pastes, improve our solder paste incoming inspection steps, re-define our stencil requirements and the following questions are open. Two questions, 1- Is anybody using/requiring 1000 Kcps or more
Electronics Forum | Thu Oct 24 10:05:59 EDT 2002 | Yannick
I don't know the name of the flux. but is a no-clean solder paste.
Electronics Forum | Fri Oct 25 05:43:14 EDT 2002 | hanvictor
i have the experience like that, it should have something to do with solder paste.
Electronics Forum | Fri Jun 23 10:10:15 EDT 2006 | Gman
Some amount of voiding was always seen on sites where solder paste is printed. These voids are much smaller. However the site where a flip chip is flux dipped has never had problems with voiding. Macro voids (and huge ones at that)across the board s
Electronics Forum | Tue Jan 31 10:59:55 EST 2006 | carterhoward
Hi All, I�ve been doing some research on the issue of running lead-free solder paste and leaded solder paste through reflow at the same time. The point with this would be to process all standard leaded components with Lead paste while also processi
Electronics Forum | Thu Jun 22 17:47:05 EDT 2006 | davef
First, we expect voiding in imm silver to be similar to ENIG. We expect more voiding in OSP than other common solderability protection. Second, choosing a solder paste, which does not contain resins and activators that decompose at higher temperatu
Electronics Forum | Tue Dec 13 17:41:04 EST 2011 | davef
A Study Of 0201’s And Tombstoning In Lead-Free Systems, Phase II Comparison Of Final Finishes And Solder Paste Formulations http://sheaengineering.com/Documents/APEX%2008%200201s%20and%20Tombstoning%20phase%202%20paper.pdf CONCLUSION The condition