Electronics Forum | Thu May 20 03:45:22 EDT 2021 | jineshjpr
SAC305 Will be the best choice with minimum TAL, Maximum Soak Solder Profile. Surely your solder Joint strength also will be more reliable & This can pass any kind of reliable Tests.
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Mon May 12 15:13:29 EDT 2014 | emeto
Thank you guys. As we are speaking I keep examine the problem and here is what I got so far. 1. I measured the temperatures on my profile and the lead is hotter than the board. The lead goes 12 seconds earlier than the pad and is taking the solder.
Electronics Forum | Tue Dec 13 09:29:08 EST 2011 | swag
We're soon to build a lead free assembly with 0201 components. I'm not worried about placement as our machines can handle it. Any tips on printing, screens, reflow?
Electronics Forum | Fri Dec 16 18:37:10 EST 2005 | mdemos1
Hi. I am trying to understand Tg and how it relates to reflow. With the higher temperatures of lead free, we have been looking toward laminates with a Tg of 180 instead of the current 140. My question is a little more general. In either lead free
Electronics Forum | Tue May 09 14:49:57 EDT 2006 | Larry
Hey guys, Anybody having trouble with increased false contact issues in ICT after switching from lead to lead free? Our test guys keep trying to imply that the flux residues are a problem (we're using Alpha EF2202), but as the soldering process eng
Electronics Forum | Fri Nov 12 09:19:07 EST 2004 | Dave G
Good places to start: http://www.nemi.org/ http://www.lead-free.com/ Dave G
Electronics Forum | Wed Dec 14 11:06:12 EST 2011 | swag
Thanks, Dave. Really good article.
Electronics Forum | Wed May 10 00:46:32 EDT 2006 | Chris
I agree! I am using a SAC305 no clean from Alpha. I have noticed that even hand probing with volt meter leads requires me to press very hard on the pads to bust through the flux residue.
Electronics Forum | Wed May 07 10:15:46 EDT 2008 | llaerum
We are also having some issues with certain small parts. In our case this is tantalum caps and 0402 caps. We had a vendor admit after much discussion that the plating used from a particular orgin was different on the tantalums. The tehory is thatthsi