Electronics Forum | Mon May 24 04:01:10 EDT 1999 | Joe Manzur
John, We are using a well known solder paste, begining with the letter "H". (I don't want to be accused of advertising). Also, we are now using a board inverter. In the early day's however, before we purchased a board inverter, we were having to
Electronics Forum | Fri Nov 13 09:55:08 EST 1998 | Chrys
| We are experiencing 'lifting' on one or more sides of a QFP. Poor lead co-planarity has been ruled out by independent tests. Please tell me which of the two remaining failure modes is the most probrable? | | 1. Expansion of gases in vias underneat
Electronics Forum | Sun Oct 10 18:53:04 EDT 1999 | Dreamsniper
| | | | Is there an IPC Standard stating the max. number of times that a PCB can pass through a reflow or wavesolder machine without having solder mask breakdown. | | | | | | | | PCB is FR4 | | | | Solder Mask is LPI | | | | Reflow and W/S Profile =
Electronics Forum | Thu Jul 15 19:05:58 EDT 1999 | Earl Moon
| | | We have been encountering diminishing ball shear readings these past few weeks, despite the fact that we did not change any ball shear tester parameter. Our reflow parameters are also within spec limits. ( 210-220 deg C max temp. and 40-60 sec
Electronics Forum | Tue May 31 11:56:12 EDT 2005 | chunks
Hi Matt, Get definitive answers! Contamination on the HASL finish?: From the pix you posted, it looks like something fishy is going on. I�d reject them back to the board house and demand an answer. Most board houses and purchasing people will g
Electronics Forum | Wed Apr 21 02:53:33 EDT 1999 | Raul N.
25 PPM)! | | | | 1. Is there a better process to solder the leads of QFP's with lifted "minute" lifted leads still having a realiable solder joints? | | | | 2. Or has anybody tried modifying solder pads and use thicker solder paste deposit to compe
Electronics Forum | Thu Aug 10 13:12:10 EDT 2000 | Bob Willis
You may care to review the following from my Circuits Assembly page on line. "HOW FLAT IS FLAT AND DO WE NEED FLAT CIRCUIT BOARD, YES WE DO ? As production problems go there is one that keeps reoccurring time and time again. The blame is usually di
Electronics Forum | Fri Jul 04 21:09:04 EDT 2003 | ramanandkini
I have a CEM-1 PCB board with 35 microns copper. This is PCB is finished with SMOBC+HALS. We do solder SMT LEDs, but till date we do not have problems that you have listed. The LEDs are good & bright. It even passed high & low temp cycle tests (-40 t
Electronics Forum | Thu Jun 25 09:29:01 EDT 1998 | Henry Lee
| | I have a single-sided board with test vias that pass through the board. The test vias are pasted and reflowed with the SMT components on the top side. When the boards are wavesoldered, the solder coverage on the vias is spotty. Some will so
Electronics Forum | Thu Jun 25 09:29:01 EDT 1998 | Henry Lee
| | I have a single-sided board with test vias that pass through the board. The test vias are pasted and reflowed with the SMT components on the top side. When the boards are wavesoldered, the solder coverage on the vias is spotty. Some will so