Electronics Forum | Fri Feb 09 13:28:24 EST 2018 | jmedernach
Pin holes in the solder joints on various devices can be an indicator of something amiss with the solder paste itself. Solder paste storage may be a concern. Do you possibly have someone putting paste back in the refrigerator after use? Are you tr
Electronics Forum | Thu Jun 24 04:38:31 EDT 1999 | Vinesh Gandhi
Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody help
Electronics Forum | Fri Aug 09 02:03:18 EDT 2013 | manud01
Please help me with this issue. After reflow oven I am getting blow hole (even tin drop) from a pin hole in wave connections. This blow hole part has been produced by a inductive supplier.
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
Electronics Forum | Thu May 17 22:41:05 EDT 2001 | davef
Hi Bob Still getting the cushy jobs, eh? [Tennent's and McEwans are two of my favorites. "Ahh, Beer! My one weakness...my Achilles Heel, if you will..." Homer J Simpson Quote 89/114] Under "Acceptable" for "Pin-In-Hole/Intrusive Reflow Inspection
Electronics Forum | Wed Apr 04 14:29:16 EDT 2007 | rgduval
Anyone have experience wave soldering rigid flex assemblies? I've just picked up a new job from a customer; it's a rebuild for the company, but new to me. The customer had previously taken their business elsewhere due to delamination problems with
Electronics Forum | Thu Jul 21 22:14:34 EDT 2005 | Ken
Anyone else disagree with IPC-2222 for min-lead to max hole in the application of ribbon lead connector styles?
Electronics Forum | Thu May 17 07:36:40 EDT 2001 | Bob Willis
Here is a copy of a draft document on PIHR Inspection I have jotted down on a flight to Scotland yesterday, any comments suggestions etc ? I have already most of the photos for the standard but as you know there is nothing in the IPC document it just
Electronics Forum | Tue Jun 21 14:27:14 EDT 2005 | Dreamsniper
Defects will result, Your cooling rate is affected because the hot air is not circulated properly. Outgassing will appear and you'll have pin holes / blow holes, disturbed joint etc. Correct me guys if i'm wrong. Thanks
Electronics Forum | Wed Apr 04 17:40:39 EDT 2007 | davef
Rob: How do you rework blow-holes and pin-holes? PTH plating thickness SB 1 thou or greater. Epoxy is hydroscopic. So, you should control the environment and/or bake the moisture from the boards before soldering. Search the fine SMTnet Archives f