Electronics Forum | Fri Jan 30 10:29:48 EST 2009 | petep
We have a potential new customer who has special PCB requirements. I do not know a lot of details at this point, but have several questions. One of their assemblies has within it , a MID, Solid foil layer, completely isolating one side of the PCB f
Electronics Forum | Tue May 02 21:01:21 EDT 2000 | Stefan Witte
I forgot to mention the mass placement machine from Nitto. The Nitto machine places all components out of bulkfeeders. Plastic tubes are routed above the feeders pick position and into cavities of a template. The template is made for the pattern of t
Electronics Forum | Tue Aug 31 19:50:44 EDT 2004 | davef
To take our turn at keeping everyone else on the straight and narrow. For more on lead contamination of no-lead solder, look here: http://www.aimsolder.com/techarticles/Lead%20Contamination%20in%20Lead-Free%20Electronics%20Assembly.pdf [We apolog
Electronics Forum | Tue Feb 23 16:45:36 EST 2010 | dyoungquist
Davef is right on as usual. We are doing exactly what you do. Some smt with no clean paste then the plate through connectors on our selective solder machine using water soluble flux. We then clean with a ultrasonic water process. We do see the re
Electronics Forum | Wed Jan 09 15:24:49 EST 2002 | mregalia
Thanks Chris. As I was writing my last message our mailperson dropped off the latest issue of Circuit Assembly. It has an article on mixing SMT and COB on the same board. The author recommends as a compromise 10-20 micro inches of gold over 70-100 of
Electronics Forum | Mon Jun 27 09:09:19 EDT 2005 | Bob R.
We've all been soldering Pb free parts for a couple decades. All your surface mount capacitors have probably had a Sn finish for years. Whenever one of our parts with a SnPb finish converts for Pb free we have the manufacturing site do a small buil
Electronics Forum | Mon Jan 07 20:37:15 EST 2002 | davef
For soldered areas, we like to keep gold thickness substantially below the maximum you propose. Search the fine SMTnet Archives for our discussions on the topic of acceptable levels of gold with solder connections. Let�s fix this �no one seems be s
Electronics Forum | Tue Aug 31 19:17:43 EDT 2004 | russ
Now see Dave, now I have some good info on why it is "bad", This must be the lead enrichment I have heard about but never got any substantiated data or explanantion. I wonder how much weaker or less reliable these are. Is there any data that you k
Electronics Forum | Tue Feb 14 22:48:06 EST 2006 | Cal Kolokoy
That is a tough situation and a tough answer for us SMT forum participants. After all, most of us are in the business of placing and soldering components to circuit boards, and you know the saying; you can't make solder joints with an unsolderable su
Electronics Forum | Thu May 25 11:31:52 EDT 2006 | muse95
Patrick, I believe you are mistaken about this being a myth. Many component manufacturers changed more than plating to make their component withstand higher temps. Some changed mold compounds, others changed plastic types used. Many of these change