Electronics Forum | Mon Nov 07 16:31:47 EST 2005 | CW
hi Bob, Thanks for the info. I understand your comments, but I am looking for specific guidance, If I am putting chip capacitors on a .063 FR4 board, what size package should we stay away from to avoid cracking? (I realize this is dependent on h
Electronics Forum | Thu Feb 04 09:09:07 EST 1999 | dave
Can anyone help me with the pros and cons of trying to wave solder tantalum and large (1812) ceramic capacitors. I do know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what problems I c
Electronics Forum | Fri Feb 05 09:39:58 EST 1999 | Dave F
| Can anyone help me with the pros and cons of trying to wave | solder tantalum and large (1812) ceramic capacitors. I do | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what proble
Electronics Forum | Mon Sep 28 09:18:30 EDT 1998 | Ben Wilmot
The majority of SMT resistors use the following notation. 10 X eg 153 represents 1k5 resistor The third digit in the sequence denotes the number of zeros to add after the first two digits giving the value in ohms. Many Caps will follow the same nota
Electronics Forum | Wed Mar 08 16:52:07 EST 2006 | darby
Which model Yamhah are you talking about and what is the make and model # of the manifold block for the micro ejectors? If it has the Koganei ME05M series then your local rep can supply the filters. It is a good idea to get spare O-rings for the filt
Electronics Forum | Tue Feb 16 16:28:30 EST 1999 | Tuffty
| | Can anyone help me with the pros and cons of trying to wave | | solder tantalum and large (1812) ceramic capacitors. I do | | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what
Electronics Forum | Wed Mar 10 13:53:13 EST 1999 | Vincent Vega
| We will wave solder a board with SOIC14 and SOIC16 parts on the bottom. It has been difficult to find any specific wave solder process recommendations from manufacturers of the SOICs. The pad geometry utilizes theiving pads on both sides to reduce
Electronics Forum | Tue Nov 08 05:00:23 EST 2005 | rlackey
Hi CW, Regarding orientation, yes, your diagram is right - see the following link for confirmation. http://search.murata.co.jp/Ceramy/image/img/A18X/C2EB3C.PDF Regarding information on bending strength you want to talk to your local Murata office
Electronics Forum | Tue Feb 04 21:07:16 EST 2014 | sarason
You should ask yourself a bunch of questions before you consider going down this path. The first being where are the bottlenecks in your existing line and is there anything you can do to eliminate or decrease there bottleneckness (made up word). I
Electronics Forum | Fri Aug 17 10:50:15 EDT 2007 | Frank
I agree that the documentation should be used and not necessarily the silk screen. The silk screens can be a first line of defense, but nothing beats the proper documentation. Years ago I visited a contract manufacturer that a friend was working at