Electronics Forum | Wed May 20 17:00:56 EDT 2009 | dyoungquist
We just placed a 56 pin QFN, 1 per board, on 10 boards and had zero defects. A good paste job, proper placement and a correct oven profile are the keys. If these are set up correctly, on larger runs your defects won't be zero but they should be le
Electronics Forum | Tue Sep 23 23:19:34 EDT 2003 | RLW
If you have a board that you've run several times, now you run it and like before all settings are the same, but now you have 0603's randomly skewed or an inch or so away from their intended pad (as if popped up in the air), or an occasional 7343 cap
Electronics Forum | Fri Jul 15 03:29:52 EDT 2005 | dougs
thomas, why isn't it process control, you cant just think that because you've set up your machine properly ( pot temp, wave height, pre-heat etc etc )that everything is going to be ok, there are other factors that you wont find with wave riders or
Electronics Forum | Fri Jun 23 10:10:15 EDT 2006 | Gman
Some amount of voiding was always seen on sites where solder paste is printed. These voids are much smaller. However the site where a flip chip is flux dipped has never had problems with voiding. Macro voids (and huge ones at that)across the board s
Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir
Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll
Electronics Forum | Wed Mar 12 10:26:10 EDT 2008 | realchunks
Why would a board failure related problem be a process problem. I agree most companies believe EVERY problem is a Proces Problem, but in the real world we know this is not true. A pad lifting means your solder joint was able to rip it off the boa
Electronics Forum | Wed Mar 12 23:00:10 EDT 2008 | davef
You can say: The pad was lifted after reflow and prior to the dye and pry failure analysis. When we see lifted pads, we think: * That's a good solder connection * Either it took a lot of force to lift that pad or the fabrication of the board in the
Electronics Forum | Fri Feb 04 16:07:38 EST 2011 | pjc
If your peak temps in profiling the Sn/Pb solderpaste are 210C-215C, then no, you will not "weld" to the SN100C finish. SN100C is liquidus at 227C, too hot for most Sn/Pb solderpastes.
Electronics Forum | Wed Aug 23 14:59:32 EDT 2006 | bill
I�ve been lurking on the forum for a while so I will take a stab at this, mainly because there is no answer I take it that you have a variety of boards being produced at the same time and are in fixtures so the conveyors don�t need to be adjusted, a
Electronics Forum | Tue Apr 10 02:57:53 EDT 2018 | rob
Yes I would, most of our old Yamaha machines (before 2005) will do 30-35 microns @ 3 sigma with the fine camera option. Our Jukis with His res camera's will hit it too. You should be OK with most things after 1997 with the right camera choice (whic