Electronics Forum | Thu Aug 24 17:08:58 EDT 2000 | Dr. Ning-Cheng Lee
Depending on the stress condition experienced by the solder joints. For joints under a greater stress, the time to reach equilibrium can be shorter. Of course, the change is also more significant in phase structure. For low stress conditions, it may
Electronics Forum | Sat Nov 06 14:58:45 EST 1999 | Gary Moravchik
Assuming you are using Sn63/Pb37 solder paste, have you tried using a lower temp melting point solder paste for the second pass? For example, use 63/37 for first pass and a Bi58 compound solder paste for the second pass. If I recall, Bi58's melting
Electronics Forum | Wed Aug 04 18:57:26 EDT 1999 | Dreamsniper
| What oven temperature should be used to reflow solder (Sn63Pb37) on a PC board (0.075" to 0.100" thickness) in 5 to 10 minutes? | Hi Judy, In profiling you need an understanding of the reflow specs from the solder paste manufacturer then you nee
Electronics Forum | Wed Aug 04 22:35:32 EDT 1999 | ScottM
| What oven temperature should be used to reflow solder (Sn63Pb37) on a PC board (0.075" to 0.100" thickness) in 5 to 10 minutes? | D... is correct -- it's all dependent on your paste and your oven. Call your paste supplier (each one has a technica
Electronics Forum | Thu Jul 15 08:34:54 EDT 1999 | Mark Quealy
I use a Transition Automation Semi- Automatic stencil printer with laser cut frameless stencils. My solder paste is an SN63/PB37 RMA 291. I do not operate with in a controlled humidity enviroment. The room temp generally runs around 70 deg's but humi
Electronics Forum | Tue Apr 13 08:08:33 EDT 1999 | Rob Palson
We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to bu
Electronics Forum | Mon Apr 19 02:38:41 EDT 1999 | Brian Sloth Bentzen
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Tue Oct 16 17:38:42 EDT 2001 | lileubie
Depending on the type of teflon material, thickness, and reflow profile requirements, these will have a direct bearing on your maximum process allowable PCB pallet size. You'll want to be careful on how big the PCB or pallet is. Larger teflon PCBs
Electronics Forum | Sun Mar 31 22:50:28 EST 2002 | ianchan
Nope, we do not have solder beads, like we said, what we have are near perfect solder fillets except for the portion where the component is "floating OFF" the pcb pads. We are now mucking through the IPC-A-610C for specifications dictation on "tilted
Electronics Forum | Mon Apr 15 21:27:16 EDT 2002 | djarvis
Everything we do is RF and have had no problems in the last 7 years with - Indium NC-SMQ92J, Sn63 Pb 37, 90.25% Metal, -325+500 mesh. Stencils are always 0.005" thick. However I will qualify that by adding we are an OEM and each new product may requi