Electronics Forum | Fri Nov 14 10:45:22 EST 2014 | tombstonesmt
We use both types in house. We started with a board moving over the pot, slowly moved on to Jade machines and eventually Synchrodex. Like you mentioned without palletizing you'll have component movements during the cylce and most likely won't have th
Electronics Forum | Fri Jun 12 14:22:53 EDT 1998 | Ryan Jennens
| Hey all! | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pall
Electronics Forum | Wed Mar 28 19:40:14 EST 2001 | Rob Fischer
Try a search engine and look up "+solder+pallet". Any of the major pallet manufacturers can supply this or any other composite materials that you may be looking for. Of course (as I am employed by EMC) I would prefer you choose my site. Try to kee
Electronics Forum | Fri Jun 12 15:56:43 EDT 1998 | Ryan
| | | Hey all! | | | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is o
Electronics Forum | Fri Jun 12 14:31:04 EDT 1998 | Earl Moon
| | Hey all! | | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a
Electronics Forum | Mon Dec 02 17:02:28 EST 2002 | Vince Whipple
Steve, I agree with the recommendation to check the temperature. This is the first place to go. Is this an IPA or water based Noclean? What is the topside temp of the assembly at the effected areas? If you are too cold you will have a tendency to hav
Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram
Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle
Electronics Forum | Mon Dec 02 18:01:12 EST 2002 | GSW
Hi, Try to check if there is water absorbed in the flux or the humidity around the wave area. possibly plating on barrels that might be damaged?
Electronics Forum | Wed Dec 04 14:09:52 EST 2002 | Vince Whipple
By the way, what type of preheaters do you have? IR? Convection? If you have IR, there may be a way to cheat. Vince W
Electronics Forum | Mon Dec 02 12:52:40 EST 2002 | slthomas
We're trying a selective soldering pallet for the first time with mixed reviews. Are solder balls a prevalent problem with this process? Most of them seem to correspond with pallet wall locations....is it too much turbulence from the rotary chip wav