Electronics Forum | Thu Dec 29 03:57:16 EST 2005 | sparrow
Hello Chris, To be honest, it's hard to believe you could not bond to ENIG at all. Yes, the gold layer is thin and hard, but it just narrows the process window and does not make the bonding impossible. I say this, because we have been using TS gold w
Electronics Forum | Mon Mar 12 09:25:16 EDT 2007 | rgraves
Our internal designers are employing SMT connectors that utilize a �PCB positioning boss� in conjunction with normal gull wing leads. The use of these devices is based on the advertised ability of the boss to prevent �mis-insertions� and assist in �
Electronics Forum | Wed Apr 25 10:37:14 EDT 2001 | davef
If you heat a BGA too quickly, the corners of the device will curl towards the ceiling [potato chip], because they come to temperature faster that other areas. Adding to this, thinner substrates tend to potato chip more and faster than thicker subst
Electronics Forum | Tue Jan 12 15:02:12 EST 1999 | Earl Moon
| I have used conductive adhesives for some time now on thickfilm. Does anyone know of a really good conductive adhesive to attach flip chips to flex circuits? I would like to stencil print the adhesive to the substrate and then place the flips chi
Electronics Forum | Tue Jan 12 15:04:40 EST 1999 | Earl Moon
| I have used conductive adhesives for some time now on thickfilm. Does anyone know of a really good conductive adhesive to attach flip chips to flex circuits? I would like to stencil print the adhesive to the substrate and then place the flips chi
Electronics Forum | Wed Sep 30 11:57:19 EDT 1998 | Manish Ranjan
Hi Everybody Is anyone aware of the possible causes that may lead to voids in the solder bumps after assembly. We assembled some dice on thin substrates and after assembly, void formation in the solder bumps were observed. We have already trie
Electronics Forum | Wed Sep 30 11:56:46 EDT 1998 | Manish Ranjan
Hi Everybody Is anyone aware of the possible causes that may lead to voids in the solder bumps after assembly. We assembled some dice on thin substrates and after assembly, void formation in the solder bumps were observed. We have already trie
Electronics Forum | Wed Aug 12 07:31:37 EDT 1998 | Earl Moon
| We are taking enquiries for sub-contract work that we hope to be doing by Christmas. One of the enquiries is to assemble chip capacitors and an SO14 onto ceramic. Does the printing process, paste used and reflow process remain the same, or are ther
Electronics Forum | Mon Apr 01 23:16:44 EST 2002 | dwoon
Hi, Heard about flux encapsulant - a compression-flow flux and underfill product for flip chip assembly. It eliminates the need for a separate underfill operation. Does anyone has experience in actual production run? What is the possible effect for
Electronics Forum | Mon May 12 10:48:49 EDT 2003 | Theresa Woodford
Does anyone have any experience with plasma cleaning? I currently have an IMS Substrate (10-15 microinch gold flash over electroless Ni) attched to Ryton PPS / R40 walls (40% glass filled/compression molded). The wall is being attached to the IMS u