dear all, update: we got that the calibration of SIM is the problem, the distance between SIMs need to be calibrated. can someone help us get the manual that describe on how to calibrate the SIMs? we have a problem with our cyberoptics AOI machine
Electronics Forum | Thu Nov 06 12:25:42 EST 2014 | arifa_anees
Rush PCB Provide their customers with printed circuit board assemblies, electronic assemblies, medical assemblies, and box-builds that are built to customer specifications at the most competitive prices while maintaining the highest quality of workma
Electronics Forum | Fri Oct 22 11:37:38 EDT 1999 | Brett Gordon
Working DFM SMT issues with respect to a client's artwork together with a heavily modified solder stencil, I was able to reduce 0402 tombstoning from 80% across the board to 3%. I winged the aperture reductions, but are there any "rules" or guidelin
Electronics Forum | Fri Oct 22 21:23:59 EDT 1999 | se
Tombstoning is usually oven profiling, see October 14 thread below. Aperture rules are misleading. Component mix, stencil thickness, paste factors, all contribute. Also, are you making the stencil from a paste or pad layer or from a soldermask layer?
Electronics Forum | Tue Feb 04 08:32:49 EST 2003 | roertner
In my experience AOI's are good for checking machine setup I.E. first piece inspection. After that the only things they will typically catch are wrong parts, reversed parts, missing parts, and tombstones. I would however suggest getting an AOI with a
Electronics Forum | Sun Dec 21 04:27:44 EST 2014 | leadthree
Are you really sure that related to my issue? Anyway, in the meantime I experimented a bit with a PVC supplier and now I have a soft PVC that can handle my 185°C (365°F) for 90 Minutes. It becomes a little bit yellow - the previous got cat-black.
Electronics Forum | Wed Sep 29 08:26:03 EDT 2010 | babe7362000
We are Currently running a Board and it seems that the SOT-223's on the bottom side have flux and water trapped under the part. Nothing has changed in our process and this is the only board that it is happening on. We are using Kester R562 water wa
Electronics Forum | Tue Aug 28 12:25:26 EDT 2001 | Steve
To be honest with you, it doesn't really matter how you present the data, as long as you understand what the problems are. Bottom line is who cares what the numbers are unless you are doing something about it. Are you able to track the individual de
Electronics Forum | Tue Aug 28 13:46:46 EDT 2001 | mparker
To clarify on "Opportunities"- With 1000 components, the opportunities are far greater than 1000. You have 1 opportunity per component for a component defect i.e. bent lead, damaged part, tested bad, etc. You have a second opportunity per component
Electronics Forum | Tue Aug 15 07:02:13 EDT 2000 | George Verboven
We are assembling SMD-Leds (Chip LED cl-220yg-c-ts)on flex foil with Electrical conductive glue (Matthey A1401). When we investigated these foils we found cracks between the conductive adhesive and round the edge of the Chip-leds. This cracks cause f