Electronics Forum | Thu Jul 03 08:40:23 EDT 2003 | Kris
Hi, undercured solder resists may be a defect people have seen so far. Some of the probles arising is blistering as well as reaction with wave solder flux that may lead to some kind bad gel like formations. Gels the idea would be to reflow the ba
Electronics Forum | Thu Jul 03 07:59:53 EDT 2003 | loz
OK. Point taken, lets keep this simple then, how about just the issue of under cured solder resist? Any body else encountered such issues. Just feedback, 'cause its something that just seems to have been highlighted to me. Thanks.
Electronics Forum | Thu Jul 03 17:42:01 EDT 2003 | Kris
What have you not seen ?
Electronics Forum | Sun Sep 05 03:52:11 EDT 1999 | Brian
| We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these sizes
Electronics Forum | Thu Jul 03 03:23:04 EDT 2003 | loz
I have been advised recently about pcb manufacturers, that somehow or other supply pcb's with contamination. Visually they are fine, but problems arise during SMT manufacture, ie solder balling, non-wetting on pads, and also during wave solder proces
Electronics Forum | Thu Feb 04 09:09:07 EST 1999 | dave
Can anyone help me with the pros and cons of trying to wave solder tantalum and large (1812) ceramic capacitors. I do know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what problems I c
Electronics Forum | Fri Feb 05 09:39:58 EST 1999 | Dave F
| Can anyone help me with the pros and cons of trying to wave | solder tantalum and large (1812) ceramic capacitors. I do | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what proble
Electronics Forum | Thu Jul 03 11:32:38 EDT 2003 | dphilbrick
It might be easier to answer what we haven�t seen. In today�s economy everyone is looking for a deal. Just remember "there is no sex in the Champaign Room"
Electronics Forum | Tue Aug 26 13:44:14 EDT 2008 | cgray
The chain and fingers for our Wave solder is getting a large amount of residue from the flux (high dissolved solids) we are using. Any recommendations for products that can clean polymerized flux.
Electronics Forum | Fri Sep 03 03:56:41 EDT 1999 | Wolfgang Busko
| We've noticed that there are many different recommendations for pad sizes for various SMT parts. This seems to vary wildly from manufacturer to manufacturer for the same case sizes. Is there any standards that can used used to specify these sizes
.gif)