Electronics Forum | Fri Feb 19 06:45:29 EST 1999 | Charles Stringer
Does anybody have any reliable alternatives to device bake out for plastic bodied components. We do not use a whole package at time and therefore have to oven bake the balance before we can use them. I have come accross dry nitrogen storage chambers
Electronics Forum | Thu Apr 16 14:31:04 EDT 1998 | Lou Madge
Dear Colleague, A seminar titled "Things that you should know before selecting an alternative surface finish" will be offered on Friday , April 24 in Philadelphia (during the Nepcon East week). The seminar will be covering topics related to the SERA
Electronics Forum | Mon Apr 20 13:49:49 EDT 1998 | Gordon Wenker
| Dear Colleague, | A seminar titled "Things that you should know before selecting an alternative surface finish" will be offered on Friday , April 24 in Philadelphia (during the Nepcon East week). | The seminar will be covering topics related to th
Electronics Forum | Thu Apr 16 14:29:07 EDT 1998 | Lou Madge
Dear Colleague, A seminar titled "Things that you should know before selecting an alternative surface finish" will be offered on Friday , April 24 in Philadelphia (during the Nepcon East week). The seminar will be covering topics related to the SERA
Electronics Forum | Tue Dec 17 08:38:30 EST 2002 | Randy Villeneuve
Jim, In most cases if you can eliminate a process you will save money. With that in mind, an all surface mount or all through hole design is prefered. There are alternatives to that rule, like hybrid designs that can be pin and paste soldered. It al
Electronics Forum | Fri Dec 31 10:22:54 EST 2004 | gpaelmo
I agree that something has to be done with the lead waste but I believe that a recycling program is a better alternative to lead-free. Isn't silver more toxic? How about the venting of alternate alloy fumes, let alone the effects on operators. I say
Electronics Forum | Thu Jun 23 10:43:40 EDT 2005 | davef
It wouldn't surprise us [too much] if this part wouldn't stay for second sided reflow. * If the lead contact area to weight is less than 44 gm / inch^2 [we know the units are goofy, but convient], it'll stay. * Alternately, just run a scrap board a
Electronics Forum | Tue May 30 10:55:57 EDT 2006 | bryanhewson
I am a lay person researching the application of non-woven material in stencil rolls either using branded material or non-branded alternatives for DEK, MPM Panasonic machines in SMT environments. I have read a number of articles referring to aqueous
Electronics Forum | Mon Feb 18 03:40:04 EST 2008 | akareti
Hi everybody, I found a defect varistor 0603 Tombstone and poor welting when we use component that terminal is Silver palladium (Ag/ Pd) with Leaded solder paste (63/37). Then we change alternative component that terminal is Ni/ Sn the result not fou
Electronics Forum | Thu Apr 15 20:01:24 EDT 2010 | sarason
I normally use a particularly aggressive Hand Cleaner for cleaning oil off your hands at garages/ workshops and then Benzotriazole. The Hand cleaner comes from an industrial chemical supplier. It usually contains some NaOH while most Hand-cleaners do