Electronics Forum | Wed Jul 18 08:44:20 EDT 2012 | leeg
We use the Edding pen as stated but then apply a quick set epoxy resin over the top and allow to dry, this does work.
Electronics Forum | Wed Jul 18 08:48:26 EDT 2012 | mccabekev
How are you applying the expoxy resin? Why use the expensive pen edding aerospace pen under the epoxy when a cheaper pen will do?
Electronics Forum | Tue Feb 19 13:31:28 EST 2019 | SMTA-Joe
I have seen this issue with manufacturer markings stamped on PCBs. The ink just melts away as soon as CC touches it.
Electronics Forum | Thu Dec 10 15:33:55 EST 2009 | duso02
We use one quite often. Our machine is a Uvitron Conveyor 40 as we are a large coating house and this allows us to process many boards. Dymax also maufactures and sells machines as well. Humiseal and Dymax both manufacture UV coatings. Emerson Cuming
Electronics Forum | Mon Dec 27 10:03:35 EST 2010 | duso02
Contact your distributor for the coating or Humiseal directly. Humiseal has had a recent issue with batches of 1B31. The specific problem is lack of adhesion, which is what you have as well. You need to find out if your batch # is one of the affected
Electronics Forum | Mon Feb 18 18:13:30 EST 2019 | slthomas
Has anyone found a durable, indelible inspection stamp ink? We have an extreme case of smearing/obliteration because we have the boards dip coated (Humiseal 1B73). The manufacturer of our stamps is zero help, i.e., the best I could get out of them
Electronics Forum | Fri Apr 22 10:12:14 EDT 2005 | davef
Common RTV does out-gas causing corrosion. NASA allows use of non/low-out-gassing RTV. Try the following companies: * Ablestik Electronic: Materials, 20021 Susana Road, Rancho Dominguez, California 90221 U.S.A., 310-764.4600, F 310-764-2545 * Arlon
Electronics Forum | Tue Feb 19 14:07:29 EST 2019 | slthomas
I figured it was just going to take a little searching to find a (more expensive) stamp that used an (more expensive) indelible ink. Not the case. Just can't find anything at all, and the stamp manufacturers say not to use any ink but what they provi
Electronics Forum | Thu Apr 28 11:14:27 EDT 2005 | bbarr
If you apply the RTV after coating, what happens to bond strength since you are now bonding to the coating and not the board? Will the caps still survive vibration and shock? I specify applying RTV before coating for this reason. Am I correct? I als
Electronics Forum | Sun Dec 26 23:48:01 EST 2010 | raghu
Dear Sir, We are using 1B31 conformal caoting of 48 sec viscosity in Zahn #1 cup, by machine(PVA354) application with Tank air pressure 2.3 psi, automising air pressure 1 psi. 7 days after application we are observing peeling off problem.. And n
Lewis and Clark is your #1 Pre-Owned Surface Mount and In-Circuit Test equipment supplier. We offer a variety of equipment solutions at a significant cost savings over new.
Manufacturer / Equipment Dealer / Broker / Auctions
18 Celina Ave., Unit 16
Nashua, NH USA
Phone: (603) 594-4229