Electronics Forum | Mon Jul 06 20:32:34 EDT 1998 | Chiakl
Hi there, I am looking for some informations concerning the shear or pull strength of a typical TQFP 20 mils leads in relationship with the Copper/Tin intermetalic layer thickness. Could anyone help? Thank in advandce. rgs, chiakl
Electronics Forum | Thu Jul 09 21:04:50 EDT 1998 | Dave F
| Hi there, | I am looking for some informations concerning the shear or pull strength of a typical TQFP 20 mils leads in relationship with the Copper/Tin intermetalic layer thickness. Could anyone help? | | Thank in advandce. | rgs, | chiakl Chiakl
Electronics Forum | Fri Mar 24 12:16:37 EST 2006 | patrickbruneel
Darn Rob you're brilliant You just solved the dilemma of micro cracks and hot tear in lead free, just add a softer metal like.....and the joints won't crack. You wrote "BTW: Lead is far softer & dissolves far more easily than copper or tin, hence wh
Electronics Forum | Wed Sep 18 06:53:05 EDT 2002 | CH
1) For solder short, pls check the paste height. Too much vol will cause short. For 15 mils use 5 mils thickness stencil if possible. Check profile preheat time to prevent hot slumpof the paste. 2) type 4 powder will be better for 15 mils pit
Electronics Forum | Thu Aug 13 12:55:46 EDT 1998 | Dave F
| Hi, can you please tell me how to make green coating and through-hole plating of PCB? Thanks! | Xingsheng Xingsheng: Welcome. Bible on PCB fabrication: Printed Circuits Handbook, Clyde Coombs, McGraw-Hill Web resources: http://www.pwbrc.org/ a
Electronics Forum | Fri Mar 24 11:54:18 EST 2006 | Rob.
Hi Patrick, I'm patriotic to a point & that doesn't include supporting crap decisions, & those that have handled the ROHS & WEEE implementation have been beyond useless & should be locked in a lead lined room with Roman plumbing. Yes we need to r
Electronics Forum | Fri Jul 13 11:33:54 EDT 2007 | realchunks
Just starting and already responsible for product quality and machine adjustment? Wow, you poor bastard. Ok, I will assume this problem happens on the bottom side of the board with a thru-hole IC. The short occurs on the side that doesn't have the
Electronics Forum | Fri Apr 06 04:10:25 EDT 2001 | kensmoke
We recently had a multi block panal change at the vendor Now the production lines are producing solderability defects in great number. The makeup of the pcb is a type of fiber glass mask green in color and pads with no tinning just copper lands.
Electronics Forum | Tue Jun 11 22:06:06 EDT 2002 | scottxiao
I encounter the problem, it is easy for pad(copper) to drop off from the PCB, which is Ni/Au finish. so my question is whether there is any specification about the force between pad and laminate material, and does the PCB corpoartion test this parame
Electronics Forum | Fri Jul 24 23:20:11 EDT 2009 | umar
Hi Dave, Thanks on your feedback, May I know the how's the contributing of Moisture content of bare board and the Thickness of the copper plating in the PTH to the solder ball and solder splash during hand soldering process ?