Electronics Forum | Tue Jun 11 22:06:06 EDT 2002 | scottxiao
I encounter the problem, it is easy for pad(copper) to drop off from the PCB, which is Ni/Au finish. so my question is whether there is any specification about the force between pad and laminate material, and does the PCB corpoartion test this parame
Electronics Forum | Fri Feb 13 11:46:23 EST 2004 | Jack
Is your customer trying to reduce voiding? If the device is using Sn90 / Pb10 and the paste is Sn63/Pb37 the board will melt first. However, if both solders are 183C eutectic, it's a tossup? PCB design, copper weight, bga type (pbga, micro bga, Tbg
Electronics Forum | Tue Jun 08 08:40:37 EDT 1999 | Wister
Hi,my master How to iron out such soldering bridge with below conditions: 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB 3.using spraying fluxer and no-clean fl
Electronics Forum | Tue Jun 08 08:38:15 EDT 1999 | Wister
Hi,my master How to iron out such soldering bridge with below conditions: 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB 3.using spraying fluxer and no-clean fl
Electronics Forum | Fri Mar 20 05:55:24 EDT 2020 | yuaanliie
The gold plating on PCB has a 40% higher resistivity, and it is much more expensive. So gold is not used instead of copper for conductors. Last month I purchased some PCB from Cplfpc and Greatpcb.
Electronics Forum | Sat Jul 02 10:27:19 EDT 2022 | madisreivik
Hello ! I got exp only with leadfree HASL, but maybe the same problems apply. Also, the leaded HASL has probably lower process temperature. This could be copper, which has settled to the tank bottom. With leadfree, the copper is removed from molten
Electronics Forum | Thu Dec 07 07:36:15 EST 2006 | callckq
Hi Davef, The BGA pad is with ENIG finish, the PCB pad is with immersion silver and the solder paste is with SAC type. I already checked, the solder paste Cu is just 0.5%..Hence, I am guessing that copper migration is from PCB pad. No way it is fr
Electronics Forum | Wed Feb 26 04:28:39 EST 2014 | chongns
Hi All member I have a problem on the stable down the color of the white solder mask PCB. first, i tough the color differences was cause by the solder mask ink, but after a close look, the color change are cause by the copper under the solder mask
Electronics Forum | Tue Dec 23 11:55:37 EST 2003 | Marc Simmel
Details, details: 1) The metal shell is part of the component body. The base metal is austenitic stainless steel (304) that has been plated with 90/10 tin-lead over nickel (semi-bright). 2) The entire part (leads and shell) is elevated by the mass o
Electronics Forum | Fri Jan 29 04:39:31 EST 2016 | thaneshsivanadian
Due to the imbalance of copper distribution between top and bottom side of PCB, may cause war-page after reflow?
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830