Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram
Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle
Electronics Forum | Mon Dec 16 16:35:55 EST 2002 | Jim Ferris
Randy, Steve & all, Can you guys point me in the right direction when it come to using selective wave soldering...I am trying to get in-depth information on the Pro's & Con's of having our supplier use this process for our PWA's. (I can see there ar
Electronics Forum | Wed Jul 27 16:27:57 EDT 2005 | GS
It may be you should look for higher TG of Durapol Rgds GS
Electronics Forum | Wed Aug 27 08:00:33 EDT 2008 | cgray
We are using Multicore (MFR 301) from Henkel.
Electronics Forum | Wed Aug 27 14:07:42 EDT 2008 | cgray
Thanks for your experiences.
Electronics Forum | Tue Aug 09 13:51:03 EDT 2005 | patrickbruneel
You can also insert a stainless steel screw the size of the hole in the board before wave soldering, this will prevent the solder from wicking up to the top or close the hole (this is real cheap). I still remember the good old days using toothpicks t
Electronics Forum | Tue Dec 10 14:10:38 EST 2002 | Randy Villeneuve
Steve, I wave solder most if not all our boards with selective wave pallets. I did not catch if the solder balls were on top of the board or on the bottom but that will make a difference on what to do to get rid of them. Pallets are good and bad. On
Electronics Forum | Fri Dec 06 18:13:15 EST 2002 | slthomas
We only have solder balling problems in the interface of the pcb with the selective soldering pallet. All other boards (single, and double sided glue and waved alike) are fine, so I'm not thinking this is going to follow the normal path for resoluti
Electronics Forum | Wed Jan 26 20:52:06 EST 2005 | Chua
Hi, I'm going to evalute new solder paste and flux for wave-solder. Appreciate you could advise what are the things need to look out during the evalution. Any recommend step or proper way of doing solder paste and flux evalution. Appreciate your he
Electronics Forum | Mon Dec 02 18:01:12 EST 2002 | GSW
Hi, Try to check if there is water absorbed in the flux or the humidity around the wave area. possibly plating on barrels that might be damaged?