Electronics Forum | Thu Oct 11 19:31:58 EDT 2007 | davef
We'd probably hand solder these coils with low residue fluxed wire solder, after cleaning.
Electronics Forum | Wed Jul 12 18:25:23 EDT 2006 | George
Hi everybody: I really need your expertise on this one. I was told that the flux 270WR from AIM is either No-clean or WS soluble depending on your needs. I read the TDS and it looks like it is....but..... Is there anybody out there using this or s
Electronics Forum | Thu Nov 11 17:53:59 EST 1999 | Jeff Tamagi
I have read in some magazine articles that there is poor signal to noise ratio of RF devices when no-cean solder is used. The frequecies used exceed one Mhz? Is this true?
Electronics Forum | Wed Feb 07 07:58:58 EST 2007 | ayelet
Thank you guys. So to summarize - no spec, just need to have decent cleaning... Are you familiar with dust events that caused burning of test stations ? Thanks Ayelet
Electronics Forum | Mon Feb 05 11:31:37 EST 2007 | davef
While you're waiting for others to reply, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=19507
Electronics Forum | Tue Mar 30 06:27:22 EDT 2010 | ristikas
It happens on the middle of the stecil cleaning. The camera and the cleaner will stay under stencil in half way back. Then machine asking the initate the motors. If to press initate then the pcb stopper will hit the rails. Usually we move camera and
Electronics Forum | Tue Mar 25 08:29:33 EDT 2014 | sara_pcb
Please refer the attached jpegs, The problem is noticed after reflow soldering followed by conventional through hole soldering. Flux used one is MIL Std. Brush cleaning in IPA is followed after each soldering step. regards, R.Saravanan
Electronics Forum | Wed May 21 13:59:19 EDT 2008 | pjc
Here's what I've seen for no-clean flux applications: Leaded: Dwell Time is? 2 - 3 seconds Top side board temp max? If some small SMT parts reflow are we too hot? 110 to 120C top side board temp just before hitting the wave(s) Pot temp. 245C Lea
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Tue May 23 12:18:25 EDT 2000 | mike weekes
Which companies would you consider for protective coatings, (conformal coating) and other levels of protection? I am taking a fresh look at alternatives. Know any good tests for testing compatability of coating with flux - aqueous or no clean? SMT