Electronics Forum | Mon Nov 30 15:27:07 EST 2020 | williamrobbins
Go to the "manual" tab and change the shape of your search area to square or whatever shape you need. When you go back to "Auto" that search area should still be whatever shape you chose while in manual mode. Hope this helps.
Electronics Forum | Wed Mar 02 12:39:02 EST 2022 | stephendo
Go with the machine manufacturer's recommendations. And remember there are no hard and fast keep out areas. You can go a little tighter than they suggest but it is risky.
Electronics Forum | Tue Jan 30 14:27:17 EST 2024 | redspare1
I'm in the USA. Yes, we are going to self support or use other old machines to get this going. Which speedprint / Europlacer would you recommend?
Electronics Forum | Wed Nov 28 05:54:04 EST 2018 | robl
You need to look at what other smaller companies are using, the KY machines usually go in multiples into large installations. I've seen a few places with 1 or 2 machines but they are usually running volume of very few board types. In these environm
Electronics Forum | Sun Nov 21 13:48:16 EST 1999 | Steve Thomas
We're going to 5 mil foil from 6 mil, with a 10 mil aperture, radiused corners. Supposedly going to traps. from right angles, but who knows? We've got temp. controlled at ~73F, but no RH control. We are going to also try out a more humidity toleran
Electronics Forum | Wed Oct 06 10:31:05 EDT 1999 | Chris May
Hopefully, everybody suffers from solderability of SOT-23 devices and I would like to know how everybody else resolves this problem. Historically, here, we have always gone for 6 thou stencils. I found that going to an 8 thou stencil improved the sit
Electronics Forum | Sat Nov 07 18:01:55 EST 1998 | Jeff Sanchez
Hey All, I just noticed after all my frustration that when you go to the BETA site provided by this server that it is not the same. In other words if you play with your e-mail and then try to go to the forum you will get no where? I thought for a
Electronics Forum | Wed Jun 10 18:44:58 EDT 1998 | Earl Moon
| Okay, here's a stupid question. What exactly is HASL and OSP? We are going to delve into this technology where I work and I want to utilize the wealth of knowledge here to make life easier. Specifically, what are the differences, the advantages, di
Electronics Forum | Mon Apr 29 09:54:46 EDT 2002 | davef
MadReindeer If this white residue is salt, * Why do you say is the presence of it 'not dangerous it only looking bad'? Don't salts sometimes go into solution with moisture on the board from humidity in the air and form cathodic plating shorts betw
Electronics Forum | Thu Oct 24 17:23:12 EDT 2002 | slthomas
The logical course seems like you would just back off on the shot size or go with a smaller diameter nozzle, but if this is something new and you've been running fine up until recently then something has changed. Check the condition of your nozzles.