Electronics Forum | Thu May 13 09:52:34 EDT 2021 | winston_one
Want to update this question a little, I know it appears few years ago, but I hope there is some updates... We have to assembly few samples of motherboards with this kind of finish (customer mistake during pcb order). Normally we can use leaded sold
Electronics Forum | Wed Apr 09 13:30:20 EDT 2003 | davef
In order to get reliable reflow, you need to be at or higher than [liquidus + 20*C] for about 5 to 10 seconds. [I said 25* in a earlier post, but in an effort to stay on message, I'll stick with 20*] Don't forget that your liquidous is probably NOT
Electronics Forum | Tue Oct 03 17:04:07 EDT 2006 | cuculi54986@yahoo.com
Glenn, What alloy are you using for Pb-free HASL? You say tin copper nickel, but is it SN100C? Against manufacturing engineering's recommendation, my company specified simply "Pb-free HASL" as the finish for our Pb-free PCBs. One of our suppliers
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Mon Dec 11 20:44:37 EST 2006 | davef
Title : LEAD-FREE WAVE SOLDER FLUX EVALUATION Author : Michael Havener Author Company : Benchmark Electronics, Inc Date : 09/25/2005 Conference : SMTA International Abstract : The European Union�s deadline to ban lead in electronic pr
Electronics Forum | Tue Apr 30 07:49:38 EDT 2002 | johnw
shawn, define what you mean by solder ball's scattered across the board? I'd tend to agree with the thoughts of too much paste on chip's but normally your ball's would be mainly around these devices although som can move around depending on the surf
Electronics Forum | Wed Dec 09 10:02:10 EST 1998 | Earl Moon
| Does anybody out there have any special insights into utilizing no clean paste in high frequency RF applications? I would imagine there may be some issues with solder balls that would affect functional test (Earl, do you have something for me here?
Electronics Forum | Mon Jul 21 08:34:44 EDT 2003 | Don Bell
Blow holes/ pin holes in solder joints are the result of multiple root causes. Suggested analysis might look like this; 1) What method of solder preservation is used on the bare board. (hasl,enig, osp, etc.) HASL can leave unwanted flux residues,
Electronics Forum | Wed Mar 11 11:05:06 EST 1998 | Earl Moon
| I am having a problem with Entek coated boards. The solder past seem to just ball up on the pads. I had no problems with the board when it was hot air leveled. The board is double sided surface mount. I have tried adjusting the oven profiles mak
Electronics Forum | Thu Aug 26 10:28:07 EDT 1999 | Stuart Adams
What are the key steps to achieving high yield with CSP ??? (We are trying qualify vendors for volume fab/assembly of some products which use several CSP devices on each side of the board. (Some with 0.5mm ball pitch)) Looking through the forum I